SABIC® HDPE CLARENE 3H677
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pWi8Bh_SABICHDPECLARENE3H677.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® HDPE CLARENE sets a new standard in optics and aesthetics on brightness. SABIC® HDPE CLARENE 3H677 is a material with a specific molecular weight distribution, typically used for blow moulding of light weight and UN certified cans from 2 until 20 liters. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.952 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | < 0.10 | g/10 min | ISO 1133 |
| 190°C/21.6 kg | 9.0 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 0.35 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance (10% Igepal CO-630, Compression Molded, F50) | 200 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 61 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 1000 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 2.00mm, molded | 25.0 | MPa | ISO 527-2/1BA/50 |
| Fracture, 2.00mm, molded | 37.0 | MPa | ISO 527-2/1BA/50 |
| Tensile Strain (Break, 2.00 mm, Compression Molded) | > 1000 | % | ISO 527-2/1BA/50 |
| Flexural Modulus (2.00 mm, Compression Molded) | 1150 | MPa | ISO 178 |
| Flexural Stress (2.00 mm, Compression Molded) | 26.0 | MPa | ISO 178 |
| ESCR (Strain Hardening) - Gp | 23.0 | MPa | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Enthalpy Change | 200 | J/g | ISO 11357-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/A | ||
| -30°C, molded | 15 | kJ/m² | ISO 180/A |
| 23°C, molded | 18 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 79.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 127 | °C | ISO 306/A |
| Melting Temperature (DSC) | 132 | °C | ISO 11357-3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 883 TFE 20 | RTP Company | Acetal (POM) Copolymer | RTP |
| Sinvicomp SRP3704UV | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Torlon® 4601 | Solvay Specialty Polymers | PAI | Torlon® |
| CP PRYME® Polypropylene PPC100-35M | Chase Plastics Services Inc. | PP Copolymer | CP PRYME® Polypropylene |
| Polimid B AV Y | Poliblend S.p.a. | Nylon 6 | Polimid B |