Terblend® N 3154
| Category: | ABS+Nylon , Acrylonitrile Butadiene Styrene + Nylon |
| Manufacturer: | INEOS Styrolution Group GmbH |
| Trademark: | Terblend® N |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pVG2yy_Terblend-N-3154.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Terblend N 3154 is an 8% mineral filled ABS/PA blend with good dimensional stability and enhanced rigidity. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.11 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 8.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.60 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 3.9 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2700 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 55.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield, 23°C | 2.9 | % | |
| Break, 23°C | 35 | % | |
| Flexural Modulus | 2500 | MPa | ISO 178 |
| Flexural Stress | 80.0 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Elongation - MD (Break) | 35 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 6.0 | kJ/m² | |
| 23°C | 8.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 100 | kJ/m² | |
| 23°C | 150 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 5.0 | kJ/m² | |
| 23°C | 7.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 97.0 | °C | ISO 75-2/B |
| 1.8 MPa, Annealed | 83.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 130 | °C | ISO 306/A50 |
| -- | 105 | °C | ISO 306/B50 |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.015 | ||
| 1 MHz | 0.015 | ||
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 250 to 285 | °C | |
| Mold Temperature | 80.0 | °C | |
| Injection Velocity | 40 | mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SRF3704UV | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Moplen EP348U | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| GLAMIDE® TY-102ND | TOYOBO America, Inc. | Nylon 6 Elast | GLAMIDE® |
| K-Bin Rigid PVC KB-6100 | K-Bin, Inc. | PVC, Unspecified | K-Bin Rigid PVC |
| PLEXIGLAS® Sheet Clear 2890 | Evonik Industries AG | Acrylic (PMMA) | PLEXIGLAS® Sheet |