SCHULAFORM® 9 E HI
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAFORM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pTZau4_SCHULAFORM-9-E-HI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Impact modified POM |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 5.00 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 85.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 42.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 11 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 12 | kJ/m² | |
| 23°C | 16 | kJ/m² | |
| Charpy Unnotched Impact Strength 1 | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 122 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 73.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 130 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (2.00 mm) | 44 | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.50 mm | 650 | °C | |
| 3.00 mm | 625 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.50 mm | 675 | °C | |
| 3.00 mm | 650 | °C |
| Note Message | |
|---|---|
| 1 . | at 4 J-pendulum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 203B GB 20 TFE 10 HS UV | RTP Company | Nylon 610 | RTP |
| RheTech Polypropylene F52-01 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| CP PRYME® Polyethylene PE100LLD-50M | Chase Plastics Services Inc. | LLDPE | CP PRYME® Polyethylene |
| Huafon JF-W-6020 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| MAJORIS PBT 9237 30 BV | AD majoris | PBT | MAJORIS |