ELITE™ 5100G
| Category: | EPE , Enhanced Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ELITE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pSzTyk_ELITE-5100G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Complies with:
ELITE™ 5100G Enhanced Polyethylene Resin is a copolymer produced via INSITE™ Technology from Dow Plastics. It offers excellent impact strength, good tensile and puncture properties for thick and thin gauge industrial and consumer blown film applications. This resin exhibits higher hot tack strengths than LLDPE, making it ideal for automated packaging applications. |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.920 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.85 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Puncture Energy | 5.76 | J | Internal method |
| Film Puncture Force | 64.5 | N | Internal method |
| Film Puncture Resistance | 28.3 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD | 98.5 | J/cm³ | ASTM D882 |
| TD | 98.5 | J/cm³ | ASTM D882 |
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 272 | MPa | ASTM D882 |
| 2% secant, MD | 231 | MPa | ASTM D882 |
| 1% secant, TD | 309 | MPa | ASTM D882 |
| 2% secant, TD | 256 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 11.9 | MPa | ASTM D882 |
| TD : Yield | 12.4 | MPa | ASTM D882 |
| MD : Fracture | 43.6 | MPa | ASTM D882 |
| TD : Fracture | 36.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 480 | % | ASTM D882 |
| TD : Fracture | 620 | % | ASTM D882 |
| Dart Drop Impact | 540 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 260 | g | ASTM D1922 |
| TD | 670 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 106 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 123 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 33 | ASTM D2457 | |
| Haze | 20 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：2.5 英寸 3.5in 螺杆类型：DSB II 模具间隙：70 密尔 (1.8 mm) 熔体温度：413°F 输出：模具周长的 12 磅/小时/英寸 模具直径：8 英寸 放大比：2.5:1 螺杆速度：40 rpm 冷冻线高度：37 英寸 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 204 FR XC | RTP Company | Nylon 66 | RTP |
| Durethan® BKV 130 H3.0 DUS008 000000 | LANXESS GmbH | Nylon 6 | Durethan® |
| Elastron® V V601.A90.N | Elastron USA, Inc. | TPV | Elastron® V |
| KumhoSunny PC/ASA HSC7079Z | Shanghai KumhoSunny Plastics Co., Ltd. | ASA+PC | KumhoSunny PC/ASA |
| Starex TX-0550 | LOTTE ADVANCED MATERIALS CO., LTD. | MABS | Starex |