| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pSWO4V_Generic-ABS-PC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic ABS+PC This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.10 - 1.22 | g/cm³ | ASTM D792 |
| 23°C | 1.09 - 1.22 | g/cm³ | ISO 1183 |
| -- | 1150 | kg/m³ | ISO 1183 1 |
| -- | 1.10 - 1.23 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | |||
| 260°C/5.0 kg | 5.7 - 26 | g/10 min | ASTM D1238 |
| 260°C/5.0 kg | 11 - 29 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) | |||
| 260°C/5.0 kg | 8.00 - 26.2 | cm³/10min | ISO 1133 |
| -- | 16.6 | cm³/10min | ISO 1133 2 |
| Spiral Flow | 8.30 - 68.6 | cm | |
| Molding Shrinkage | |||
| Flow : 23°C | 0.38 - 0.74 | % | ASTM D955 |
| Transverse flow : 23°C | 0.37 - 0.60 | % | ASTM D955 |
| 23°C | 0.48 - 0.60 | % | ISO 294-4 |
| Flow | 0.60 | % | ISO 2577 3 |
| Transverse flow | 0.60 | % | ISO 2577 4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.096 - 0.22 | % | ASTM D570 |
| 23°C, 24 hr | 0.088 - 0.70 | % | ISO 62 |
| Saturated, 23°C | 0.10 - 0.61 | % | ASTM D570 |
| Saturated, 23°C | 0.19 - 0.71 | % | ISO 62 |
| Saturation | 0.60 | % | ISO 62 5 |
| Equilibrium, 23°C | 0.10 - 0.40 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.062 - 0.21 | % | ISO 62 |
| Balance | 0.20 | % | ISO 62 6 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| 23°C | 108 - 120 | ASTM D785 | |
| 23°C | 90 - 121 | ISO 2039-2 | |
| Durometer Hardness (23°C) | 80 | ISO 868 | |
| Ball Indentation Hardness | 84.5 - 115 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 1850 - 3050 | MPa | ASTM D638 |
| 23°C | 1950 - 2860 | MPa | ISO 527-2 |
| -- | 2700 | MPa | ISO 527-2 7 |
| Tensile Strength | |||
| Yield, 23°C | 43.3 - 65.6 | MPa | ASTM D638 |
| Yield, 23°C | 44.7 - 66.4 | MPa | ISO 527-2 |
| Yield | 54.2 | MPa | ISO 527-2 8 |
| Fracture, 23°C | 32.0 - 63.4 | MPa | ASTM D638 |
| Fracture, 23°C | 39.7 - 55.3 | MPa | ISO 527-2 |
| 23°C | 46.7 - 60.4 | MPa | ASTM D638 |
| 23°C | 47.6 - 70.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 1.5 - 5.2 | % | ASTM D638 |
| Yield, 23°C | 3.0 - 5.8 | % | ISO 527-2 |
| Yield | 4.0 | % | ISO 527-2 9 |
| Fracture, 23°C | 26 - 100 | % | ASTM D638 |
| Fracture, 23°C | 27 - 100 | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 49 - 52 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 1880 - 2750 | MPa | ASTM D790 |
| 23°C | 2040 - 2820 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 71.4 - 98.9 | MPa | ASTM D790 |
| 23°C | 73.8 - 100 | MPa | ISO 178 |
| Yield, 23°C | 67.0 - 105 | MPa | ASTM D790 |
| Fracture, 23°C | 65.0 - 90.1 | MPa | ASTM D790 |
| Coefficient of Friction | 0.16 - 0.21 | ASTM D1894 | |
| Taber Abrasion Resistance (23°C) | 62.6 - 70.2 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.2 - 81 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 48 - 710 | J/m | ASTM D256 |
| 23°C | 9.8 - 57 | kJ/m² | ISO 180 |
| Unnotched Izod Impact (23°C) | 100 - 2200 | J/m | ASTM D256 |
| Instrumented Dart Impact | |||
| 23°C | 39.5 - 65.5 | J | ASTM D3763 |
| 23°C | 24.3 - 105 | J | ISO 6603-2 |
| Dart Drop Impact (23°C) | 36.1 - 60.9 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 89.0 - 131 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 89.7 - 131 | °C | ISO 75-2/B |
| 0.45 MPa, annealed | 97.3 - 125 | °C | ISO 75-2/B |
| 0.45 MPa | 109 | °C | ISO 75-2 10 |
| 1.8 MPa, not annealed | 79.3 - 122 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 78.9 - 117 | °C | ISO 75-2/A |
| 1.8 MPa, annealed | 103 - 120 | °C | ASTM D648 |
| 1.8 MPa, annealed | 99.0 - 113 | °C | ISO 75-2/A |
| 1.8 MPa | 96.0 | °C | ISO 75-2 11 |
| Continuous Use Temperature | 60.0 - 100 | °C | ASTM D794 |
| Vicat Softening Temperature | |||
| -- | 104 - 142 | °C | ASTM D1525 |
| -- | 93.2 - 140 | °C | ISO 306 |
| 50°C/h, B (50N) | 114 | °C | ISO 306 12 |
| Ball Indentation Temperature | 80.0 - 125 | °C | IEC 60598-1 |
| Linear thermal expansion coefficient | |||
| Flow | 6.5E-5 - 1.0E-4 | cm/cm/°C | ASTM D696 |
| Flow | 6.0E-5 - 7.6E-5 | cm/cm/°C | ASTM E831 |
| Flow | 5.8E-5 - 8.6E-5 | cm/cm/°C | ISO 11359-2 |
| Flow | 7.6E-5 | cm/cm/°C | ISO 11359-2 13 |
| Lateral | 7.1E-5 - 8.3E-5 | cm/cm/°C | ASTM D696 |
| Lateral | 6.9E-5 - 7.5E-5 | cm/cm/°C | ASTM E831 |
| Lateral | 7.0E-5 - 8.2E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 8.0E-5 | cm/cm/°C | ISO 11359-2 14 |
| Thermal Conductivity | |||
| 23°C | 0.20 - 0.35 | W/m/K | ASTM C177 |
| 23°C | 0.18 - 0.21 | W/m/K | ISO 8302 |
| RTI Elec | 60.0 - 90.4 | °C | UL 746 |
| RTI Imp | 60.0 - 90.0 | °C | UL 746 |
| RTI | 60.0 - 90.4 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 1.0E+3 - 2.5E+15 | ohms | ASTM D257 |
| -- | 5.5E+10 - 1.0E+16 | ohms | IEC 60093 |
| -- | 3.8E+14 - 1.0E+17 | ohms | IEC 60093 15 |
| Volume Resistivity | |||
| 23°C | 1.0 - 5.0E+16 | ohms·cm | ASTM D257 |
| 23°C | 1.0E+13 - 2.5E+16 | ohms·cm | IEC 60093 |
| -- | 1.0E+13 - 1.1E+14 | ohms·m | IEC 60093 16 |
| Dielectric Strength | |||
| 23°C | 19 - 38 | kV/mm | ASTM D149 |
| 23°C | 15 - 37 | kV/mm | IEC 60243-1 |
| -- | 33 | kV/mm | IEC 60243-1 17 |
| Dielectric Constant | |||
| 23°C | 2.99 - 3.00 | ASTM D150 | |
| 23°C | 3.00 - 3.10 | IEC 60250 | |
| 23°C | 2.95 | IEC 60250 | |
| 100 Hz | 3.20 | IEC 60250 18 | |
| 1 MHz | 3.10 | IEC 60250 19 | |
| Dissipation Factor | |||
| 23°C | 4.7E-3 - 0.010 | ASTM D150 | |
| 23°C | 2.0E-3 - 0.050 | IEC 60250 | |
| 100 Hz | 5.0E-3 | IEC 60250 20 | |
| 1 MHz | 8.0E-3 | IEC 60250 21 | |
| Arc Resistance | 117 - 123 | sec | ASTM D495 |
| Comparative Tracking Index | |||
| -- | 218 - 600 | V | IEC 60112 |
| -- | 311 | IEC 60112 22 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 0.0 - 100 | mm/min | ISO 3795 |
| Glow Wire Flammability Index | 642 - 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 642 - 960 | °C | IEC 60695-2-13 |
| Oxygen Index | 21 - 35 | % | ASTM D2863, ISO 4589-2 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity | 143 - 258 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.8 - 112 | °C | |
| Drying Time | 2.7 - 5.0 | hr | |
| Drying Time, Maximum | 6.0 | hr | |
| Dew Point | -28.9 - -28.6 | °C | |
| Suggested Max Moisture | 0.020 - 0.043 | % | |
| Suggested Shot Size | 55 - 60 | % | |
| Suggested Max Regrind | 18 | % | |
| Rear Temperature | 222 - 270 | °C | |
| Middle Temperature | 229 - 275 | °C | |
| Front Temperature | 238 - 277 | °C | |
| Nozzle Temperature | 238 - 277 | °C | |
| Processing (Melt) Temp | 248 - 276 | °C | |
| Mold Temperature | 59.6 - 87.1 | °C | |
| Injection Pressure | 7.93 - 100 | MPa | |
| Holding Pressure | 50.0 - 75.0 | MPa | |
| Back Pressure | 0.0392 - 0.662 | MPa | |
| Screw Speed | 46 - 77 | rpm | |
| Clamp Tonnage | 5.9 - 6.1 | kN/cm² | |
| Cushion | 4.76 - 4.88 | mm | |
| Vent Depth | 0.052 - 0.057 | mm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic ABS+PCThis information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 78.8 - 120 | °C | |
| Drying Time | 3.0 - 4.1 | hr | |
| Suggested Max Moisture | 0.017 - 0.052 | % | |
| Cylinder Zone 1 Temp. | 180 - 230 | °C | |
| Cylinder Zone 2 Temp. | 208 - 233 | °C | |
| Cylinder Zone 3 Temp. | 229 - 232 | °C | |
| Cylinder Zone 4 Temp. | 229 - 245 | °C | |
| Cylinder Zone 5 Temp. | 228 - 230 | °C | |
| Melt Temperature | 257 - 260 | °C | |
| Die Temperature | 225 - 250 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic ABS+PCThis information is provided for comparative purposes only. |
| Note Message | |
|---|---|
| 1 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 2 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 3 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 4 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 5 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 6 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 7 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 8 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 9 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 10 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 11 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 12 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 13 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 14 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 15 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 16 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 17 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 18 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 19 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 20 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 21 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 22 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® GF8002 | Covestro - Polycarbonates | PC | Makrolon® |
| RTP 203.3D | RTP Company | Nylon 612 | RTP |
| Purell PE GF 4760 | LyondellBasell Industries | HDPE | Purell |
| Sup-tech P240 | Shanghai Suptech Engineering Plastics Co. Ltd. | PP, Unspecified | Sup-tech |
| Hifax X M1 T11 BLACK | LyondellBasell Industries | PP Copolymer | Hifax |