LNP™ LUBRICOMP™ RFN18SXS compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pSSTWE_LNP-LUBRICOMP-RFN18SXS-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP RFN18SXS is a compound based on Nylon 66 resin containing Glass Fiber, MOS2. Added features of this material include: Heat Stabilized. Also known as: LNP* LUBRICOMP* Compound RFL-4218 HS Product reorder name: RFN18SXS |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.51 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 0.15 to 0.35 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 13300 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 219 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.8 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 11100 | MPa | ISO 178 |
| Flexural Stress | 311 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.75 | ||
| vs. Itself - Static | 0.59 | ||
| Wear Factor - Washer | 45.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 3(23°C) | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 75 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 261 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 254 | °C | ISO 75-2/Af |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimoTek KM6080 | KMI Group Inc. | PBT | PrimoTek |
| Titacon® GB925 | Titan Plastics Compounds Co., Ltd. | Acetal (POM) Copolymer | Titacon® |
| NuSil R-2930 | NuSil Technology | Silicone | NuSil |
| Generic PPA - Carbon Fiber | Generic | PPA | Generic |
| KOPLA PA6 KNG1090 | KOPLA Co., Ltd. | Nylon 6 | KOPLA PA6 |