ALTECH® PA6 A 1000/109 1129-12LS
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | ALBIS PLASTIC GmbH |
| Trademark: | ALTECH® PA6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pSNAI4_ALTECH-PA6-A-1000-109-1129-12LS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALTECH® PA6 A 1000/109 1129-12LS is a Polyamide 6 (Nylon 6) product. It is available in Asia Pacific, Europe, or North America. Applications of ALTECH® PA6 A 1000/109 1129-12LS include handles and housings. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.13 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 9.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 3.0 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3200 | 1500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 85.0 | 45.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | |||
| Yield | 10 | -- | % | |
| Break | 10 | > 50 | % | |
| Flexural Modulus | 2800 | -- | MPa | ISO 178 |
| Flexural Stress | 105 | 55.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 4.0 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | No Break | -- | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 65.0 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 200 | -- | °C | ISO 306/B50 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+3 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+17 | 1.0E+12 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.50 mm | V-2 | -- | ||
| 3.00 mm | V-2 | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 12 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resblend PA/ABS | Polimarky Spolka Jawna | Nylon 6+ABS | Resblend |
| Sasol Polymers PE LT750 | Sasol Polymers | LDPE | Sasol Polymers PE |
| TEKAMID™ TB120G33 | Mando Advanced Materials Co., Ltd. | Nylon 6 | TEKAMID™ |
| BCC Resins BC 7009-2 | BCC Products Inc. | Epoxy | BCC Resins |
| Cariflex® IR0401 SU | Kraton Polymers LLC | IR | Cariflex® |