Sumitomo PP FS2011E
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Sumitomo Chemical Asia |
| Trademark: | Sumitomo PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pS9Yhm_Sumitomo-PP-FS2011E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Applications For print and lamination, adhesive tape, food packaging, cigarette packaging, etc. Characteristics High strength BOPP with excellent clarity, gloss and stiffness. Excellent processability and suitable for metallization. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.2 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | 98 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 32.0 | MPa | ASTM D638 |
| Fracture | > 19.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 9.0 | % | ASTM D638 |
| Fracture | > 160 | % | ASTM D638 |
| Flexural Modulus | 1280 | MPa | ASTM D790A |
| Flexural Strength | 34.0 | MPa | ASTM D790A |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 2050 | MPa | ASTM D882 |
| 1% secant, TD | 3700 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Fracture | 110 | MPa | ASTM D882 |
| TD : Fracture | 215 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 85 | % | ASTM D882 |
| TD : Fracture | 17 | % | ASTM D882 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 2.9 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 153 | °C | ASTM D1525 1 |
| Melting Temperature | 158 | °C | DSC |
| Peak Crystallization Temperature (DSC) | 114 | °C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 155 | ASTM D2457 | |
| Haze | 0.20 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Stretching Ratio - MD/TD | 4-7 to 7-10 | ||
| Stretching Temperature | 130 - 160 | °C | |
| Test pieces preparation condition: nozzle temperature 240 °C, mold temperature 60 °C.Film fabrication condition: extrusion temperature 250°C, output 60kg/hr, cast temperature 50°C.Standard stretching condition: MDO stretch ratio 5, temperature 145°C, TDO stretch ratio 8, temperature 157°C, relaxation 6.5%, line speed 25m/min, thickness 20µm. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 250 | °C |
| Note Message | |
|---|---|
| 1 . | 速率 A (50°C/h), 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Thermx® CG023 | Celanese Corporation | PCT | Thermx® |
| VYLOPET® EMC618P | TOYOBO America, Inc. | PBT+PET | VYLOPET® |
| ALCOM® PA6 900/8 GF10 MR20 SV1285-04MCF | ALBIS PLASTIC GmbH | Nylon 6 | ALCOM® PA6 |
| ASTAGLAS™ VH | Marplex Australia Pty. Ltd. | Acrylic (PMMA) | ASTAGLAS™ |
| COSMOTHENE® EVA KA-10 | TPC, The Polyolefin Company (Singapore) Pte Ltd | LDPE | COSMOTHENE® EVA |