HIPTEN® 21018A6
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | HIP-PetroHemija |
| Trademark: | HIPTEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pR1efm_HIPTEN-21018A6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HIPTEN® 21018A6 is low density polyethylene resin developed for production of thin blown film. HIPTEN® 21018A6 has extraordinary optical properties and very good mechanical properties, good processability and heat sealability. The addition of slip and antiblock agents results in good sliding and antiblocking properties of produced film. HIPTEN® 21018A6 has high clarity and is suitable for packaging for a wide variety of goods. HIPTEN® 21018A6 has Health Certificate issued by Institute for Health Protection of Serbia. Also, has Statement of Conformity, which declares product's conformity with the European norms for materials intended to come into contact with foodstuffs. Statement of Conformity is issued by Institute for Public Health, Maribor, Slovenia. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.921 | g/cm³ | ISO 1183/D |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 46 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 10.0 | MPa | ISO 527-2 |
| Fracture | 14.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 600 | % | ISO 527-2 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Tensile Strength | ISO 1184 | ||
| TD : Yield, 40 µm | 10.0 | MPa | ISO 1184 |
| MD : Break, 40 µm | 23.0 | MPa | ISO 1184 |
| TD : Break, 40 µm | 18.0 | MPa | ISO 1184 |
| Tensile Elongation | ISO 1184 | ||
| MD : Break, 40 µm | 500 | % | ISO 1184 |
| TD : Break, 40 µm | 700 | % | ISO 1184 |
| Dart Drop Impact (40 µm) | 120 | g | ASTM D1709A |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 40.0 µm | 135.1 | kN/m | ASTM D1922 |
| TD : 40.0 µm | 173.7 | kN/m | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 96.0 | °C | ISO 306 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 - 180 | °C |
| Extrusion instructions |
|---|
| Blow-up ratio: 2:1 to 3:1 |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XYRON™ VN30V | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| Advanced-PP 1101SC | Advanced Petrochemical Company | PP Homopolymer | Advanced-PP |
| EPO-TEK® 353ND | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| PENTAMID L GV30 H natur | PENTAC Polymer GmbH | Nylon 12 | PENTAMID L |
| LEXAN™ LUX7189 resin | SABIC Innovative Plastics | PC | LEXAN™ |