Kepital® LO-21
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Korea Engineering Plastics Co., Ltd |
| Trademark: | Kepital® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pR19KI_KepitalLO21.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Specially lubricant modified wear resistant grade. LO-21 is good for parts moving against metal. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.39 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 9.5 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow (3.00 mm) | 2.0 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, 23°C) | 60.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 26 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2450 | MPa | ISO 178 |
| Flexural Stress (23°C) | 81.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.5 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 95.0 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-1654G | Teknor Apex Company | TPE | Telcar® |
| Teslin® SP 1000 | PPG Industries, Inc. | PE, Unspecified | Teslin® |
| Estane® AG 4350 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Estane® |
| Durethan® BF 4212 00000 | LANXESS GmbH | PBT | Durethan® |
| Emulprene® 1509A | INSA | SBR, Emulsion | Emulprene® |