TOTAL Polyethylene HDPE 1285
| Category: | HDPE, HMW , High Density (HMW) Polyethylene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pOzmga_TOTAL-Polyethylene-HDPE-1285.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TOTAL Polyethylene 1285 is a high density polyethylene material,. This product is available in North America and is processed by co-extrusion molding. The main features of TOTAL Polyethylene 1285 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.950 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.070 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 9.0 | g/10 min | ASTM D1238 |
| 190°C/5.0 kg | 0.31 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| secant modulus 1 | ASTM D882A | ||
| 2% secant, MD : 20 µm | 841 | MPa | ASTM D882A |
| 2% secant, TD : 20 µm | 910 | MPa | ASTM D882A |
| Tensile Strength 2 | ASTM D882A | ||
| MD : Yield, 20 µm | 36.5 | MPa | ASTM D882A |
| TD : Yield, 20 µm | 34.5 | MPa | ASTM D882A |
| MD : Break, 20 µm | 61.4 | MPa | ASTM D882A |
| TD : Break, 20 µm | 58.6 | MPa | ASTM D882A |
| Tensile Elongation 3 | ASTM D882A | ||
| MD : Break, 20 µm | 300 - 500 | % | ASTM D882A |
| TD : Break, 20 µm | 300 - 500 | % | ASTM D882A |
| Dart Drop Impact (20 µm) | 350 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 20 µm | 24 | g | ASTM D1922 |
| TD : 20 µm | 120 | g | ASTM D1922 |
| Water Vapor Transmission Rate (38°C, 20 µm) | 12 | g/m²/24 hr | ASTM F1249 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 127 | °C | DSC |
| Additional Information |
|---|
| Film properties produced on 50 mm Alpine extruder with a 4:1 BUR, at 0.8 mil. |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| STYRON™ 665 | Americas Styrenics LLC | PS (GPPS) | STYRON™ |
| Sylvin 8805-95FR BROWN 7153 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TRIBOCOMP® PA6 TS13 | EPIC Polymers | Nylon 6 | TRIBOCOMP® |
| VALOX™ 7062HP resin | SABIC Innovative Plastics Europe | PBT | VALOX™ |
| Multiuse Leostomer® LJ-3170N | Riken Technos Corp. | TPU, Unspecified | Multiuse Leostomer® |