Zytel® RS 30G30HSL BK038A
| Category: | Nylon 610 , RENEWABLY SOURCED™ POLYAMIDES* |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® RS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pOTNkM_Zytel-RS-30G30HSL-BK038A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% Glass Reinforced, Renewably Sourced, Polyamide 610 Developed for Extrusion |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.31 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.70 | -- | % | |
| Flow | 0.20 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 2.00 mm, 50% RH) | 1.2 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 8100 | 6800 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 140 | 130 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.6 | 6.5 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 80 | 95 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C) | 12 | 16 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 207 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 50.0 | -- | °C | ISO 11357-2 |
| Melting Temperature 2 | 225 | -- | °C | ISO 11357-3 |
| Fill Analysis | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melt Density | 1.16 | -- | g/cm³ | |
| Melt Viscosity (250°C, 1000 sec^-1) | 360 | -- | Pa·s | ISO 11443 |
| Specific Heat Capacity of Melt | 2280 | -- | J/kg/°C | |
| Thermal Conductivity of Melt | 0.26 | -- | W/m/K |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Dugdale PVC Flexible Extrusion - Shore A 74 Compound | Dugdale Plc | PVC, Flexible | Dugdale PVC |
| Eporex® HIPS 828 | Eternal Plastics Co., Ltd. | PS (HIPS) | Eporex® |
| Kynar® 3312C | Arkema | PVDF | Kynar® |
| Ipethene® 600 | Carmel Olefins Ltd. | LDPE | Ipethene® |
| LNP™ VERTON™ RV007ESS compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ VERTON™ |