SAXAMID™ 126F4RZ21
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SAX Polymers |
| Trademark: | SAXAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pOSMrB_SAXAMID-126F4RZ21.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SAXAMID 126F4RZ21 is a polyamide 6 injection-molding-grade reinforced with 20 % glass fibres. This grade is equipped with a halogeneous-free and phosphorus-free flame retardant. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Viscosity Number (H2SO4 (Sulphuric Acid)) | 150 | cm³/g | ISO 307 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8100 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 124 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.5 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 6800 | MPa | ISO 178 |
| Flexural Stress 2 | 208 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 9.0 | kJ/m² | |
| 23°C | 11 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 79 | kJ/m² | |
| 23°C | 83 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 9.0 | kJ/m² | |
| 23°C | 12 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 67 | kJ/m² | |
| 23°C | 68 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed, 60.0 mm Span) | 212 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 216 | °C | ISO 306/B120 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | > 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-2 | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 600 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 mm) | 725 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP TIVAR® 88 BurnGuard | Quadrant Engineering Plastic Products | UHMWPE | Quadrant EPP |
| RTP 103CC LF | RTP Company | PP Homopolymer | RTP |
| Braskem PE IA 59 | Braskem | HDPE | Braskem PE |
| Iupilon® GMB1110 | Mitsubishi Engineering-Plastics Corp | PC+Polyester | Iupilon® |
| Karina BEIGE PVC COMPOUND -E 700-08/166-B | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |