LNP VERTON* RV00CESS is a compound based on Nylon 66 resin containing Long Glass. Added features of this material include: Easy Molding. Also known as: LNP* VERTON* Compound RF-700-12 EM HS Product reorder name: RV00CESS |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.71 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.20 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.40 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.41 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.20 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.44 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 19700 | MPa | ASTM D638 |
| -- | 23300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 270 | MPa | ASTM D638 |
| Fracture | 261 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 1.6 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 18000 | MPa | ASTM D790 |
| -- | 18900 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 289 | MPa | ASTM D790 |
| -- | 433 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 410 | J/m | ASTM D256 |
| -40°C 2 | 43 | kJ/m² | ISO 180/1A |
| 23°C 3 | 54 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 100 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 18.0 | J | ASTM D3763 |
| -- | 18.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 64.0mm span 5 | 252 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 247 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 6 | 252 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 1.8E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 1.7E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 5.4E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 5.3E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 282 - 293 | °C | |
| Middle Temperature | 288 - 299 | °C | |
| Front Temperature | 288 - 299 | °C | |
| Processing (Melt) Temp | 288 - 304 | °C | |
| Mold Temperature | 93.3 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| 6 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® AS30NT6001 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| GERMADUR KF 30 | Kunststoff-Kontor-Hamburg GmbH | PBT | GERMADUR |
| INEOS HDPE TUB 121 | INEOS Olefins & Polymers USA | HDPE Copolymer | INEOS HDPE |
| OPNYL OP66GF60 | Ovation Polymers Inc. | Nylon 66 | OPNYL |
| ULTEM™ 2310EPR resin | SABIC Innovative Plastics | PEI | ULTEM™ |