Bakelite® PF 6506
| Category: | Phenolic , Phenolic |
| Manufacturer: | Hexion Inc. |
| Trademark: | Bakelite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pMlEmR_Bakelite-PF-6506.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product Description Phenolic moulding compound, inorganically filled, glass fibre reinforced, high dimensional stability at raised temperature, good media resistance, heat- resistant, UL listed moulding compound 1.5 mm / V-0 (ALL) Application Areas Thermally and mechanically highly stressed parts in automotive field, insulating flanges, contact support power switch and switch covers |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.72 | g/cm³ | ISO 1183 |
| Apparent Density | 0.73 | g/cm³ | ISO 60 |
| Molding Shrinkage 1 | 0.30 | % | ISO 2577 |
| Water Absorption - 24h/23C | 10.0 | mg | ISO 62 |
| Post Shrinkage 2 | 0.10 | % | ISO 2577 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Molding Pressure | > 15.0 | MPa | |
| Compression Molding Temperature | 160 to 190 | °C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 450 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 14000 | MPa | ISO 178 |
| Flexural Stress 3 | 140 | MPa | ISO 178 |
| Compressive Stress | 250 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 9.5 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (8.0 MPa, Unannealed) | 190 | °C | ISO 75-2/C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength 4(1.00 mm) | 26 | kV/mm | IEC 60243-1 |
| Relative Permittivity (100 Hz) | 7.00 | IEC 60250 | |
| Dissipation Factor (100 Hz) | 0.050 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 150 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, All) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 60.0 to 75.0 | °C | |
| Nozzle Temperature | 80.0 to 100 | °C | |
| Processing (Melt) Temp | 80.0 to 100 | °C | |
| Mold Temperature | 160 to 190 | °C | |
| Injection Pressure | > 15.0 | MPa | |
| Back Pressure | 0.500 to 2.00 | MPa |
| Note Message | |
|---|---|
| 1 . | Injection |
| 2 . | Injection |
| 3 . | 2.0 mm/min |
| 4 . | short term, electrode layout P25mm/P25mm in transformer oil equivalent to IEC 60296 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCLAIR® FP120 Series | NOVA Chemicals | LLDPE | SCLAIR® |
| Nylene® 406F | Custom Resins Group | Nylon 6 | Nylene® |
| Crastin® HR5330HF BK503 | DuPont Performance Polymers | PBT | Crastin® |
| Estane® 58226 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyester | Estane® |
| LNP™ LUBRICOMP™ RAL23S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |