| PLENCO 01508 is a mineral filled pelletized polyester molding compound, which offers excellent heat resistance and electrical properties. UL recognized under component file E40654. 01508 is available in gray. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.07 | g/cm³ | ASTM D792 |
| Apparent Density | 0.94 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 0.52 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.11 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 67 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12100 | MPa | ASTM D638 |
| Tensile Strength | 52.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.90 | % | ASTM D638 |
| Flexural Modulus | 11700 | MPa | ASTM D790 |
| Flexural Strength | 87.4 | MPa | ASTM D790 |
| Compressive Strength | 139 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 25.5 | J/m | ASTM D256 |
| Notched Izod Impact | 27 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 233 | °C | ASTM D648 |
| Continuous Use Temperature | 218 | °C | ASTM D794 |
| CLTE - Flow | 6.0E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.4E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | ASTM D149 | ||
| -- 1 | 13 | kV/mm | ASTM D149 |
| -- 2 | 11 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 5.00 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.014 | ASTM D150 | |
| Arc Resistance | 184 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 600 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Additional Information |
|---|
| The value listed as Mold Shrink, Linear-Flow, ASTM D955 was tested according to the ASTM D6289 standard.The value listed as Comparative Tracking Index, UL 746 was tested according to ASTM D3638.Post Shrinkage, ASTM D6289, 72hr, 120°C: 0.01%Heat Resistance, ASTM D794: 218°CDrop Ball Impact, PLENCO Method: 172 J/m |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Shot Size | 20 - 80 | % | |
| Rear Temperature | 49.0 - 71.0 | °C | |
| Front Temperature | 85.0 - 93.0 | °C | |
| Processing (Melt) Temp | 93.0 - 100 | °C | |
| Mold Temperature | 163 - 182 | °C | |
| Injection Pressure | 6.20 - 11.0 | MPa | |
| Back Pressure | 0.300 | MPa | |
| Screw Speed | < 60 | rpm | |
| Cushion | 3.00 | mm |
| Injection instructions |
|---|
| Injection Time: 3-6 sec |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| 2 . | Method B (step by step) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REPOL® H230FG | Reliance Industries Limited | PP Homopolymer | REPOL® |
| Sarlink® TPV 3180 | Teknor Apex Company | TPV | Sarlink® TPV |
| Unichem 6811G-05 | Colorite Polymers | PVC, Unspecified | Unichem |
| PETOPLEN MH 220N | PETKIM Petrokimya Holding A.S. | PP, Unspecified | PETOPLEN |
| Plexiglas® Hi-Gloss NTA-3 | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |