IROGRAN® A 78 P 4766
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Huntsman Corporation |
| Trademark: | IROGRAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pLdU1I_IROGRAN-A-78-P-4766.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
IROGRAN A 78 P 4766 is a flame-retardant, halogen-free, thermoplastic polyether-polyurethane intended for extrusion and injection moulding applications. Additional characteristics of the product is the high flexibility and elasticity. PERFORMANCE FEATURES
APPLICATIONS
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.16 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/21.6 kg) | 110 | cm³/10min | |
| Molding Shrinkage - Flow (Injection Molded) | 1.0 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shore A, Injection Molded | 82 | ||
| Shore D, Injection Molded | 30 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion 2 | 40 | mm³ | ISO 4649 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| TMA 3 | Internal Method | ||
| High : 635.0 µm | 190 | °C | |
| Low : 635.0 µm | 165 | °C |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 4 | |||
| 100% Strain | 5.79 | MPa | ASTM D412 |
| 100% Strain | 5.20 | MPa | DIN 53504 |
| 300% Strain | 9.65 | MPa | ASTM D412 |
| 300% Strain | 8.00 | MPa | DIN 53504 |
| Tensile Strength 5 | |||
| Break | 27.6 | MPa | ASTM D412 |
| Break | 30.0 | MPa | DIN 53504 |
| Tensile Elongation 6(Break) | 800 | % | ASTM D412, DIN 53504 |
| Tear Strength 7 | |||
| -- | 71.8 | kN/m | ASTM D624 |
| -- | 40 | kN/m | ISO 34-1 |
| Compression Set 8 | ASTM D395, ISO 815 | ||
| 23°C, 24 hr | 20 | % | |
| 70°C, 24 hr | 40 | % |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 to 110 | °C | |
| Hot Air Dryer | 80.0 to 90.0 | °C | |
| Drying Time | |||
| -- | 3.0 | hr | |
| Hot Air Dryer | 3.0 | hr | |
| Dew Point | -30.0 | °C | |
| Rear Temperature | 175 to 195 | °C | |
| Middle Temperature | 175 to 195 | °C | |
| Front Temperature | 175 to 195 | °C | |
| Nozzle Temperature | 180 to 200 | °C | |
| Processing (Melt) Temp | 170 to 195 | °C | |
| Mold Temperature | 20.0 to 70.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 3.0 | hr | |
| Hopper Temperature | 25.0 to 40.0 | °C | |
| Cylinder Zone 1 Temp. | 165 to 190 | °C | |
| Cylinder Zone 2 Temp. | 165 to 190 | °C | |
| Cylinder Zone 3 Temp. | 165 to 190 | °C | |
| Cylinder Zone 4 Temp. | 165 to 190 | °C | |
| Cylinder Zone 5 Temp. | 165 to 190 | °C | |
| Adapter Temperature | 175 to 195 | °C | |
| Die Temperature | 175 to 200 | °C |
| Note Message | |
|---|---|
| 1 . | Injection Molded |
| 2 . | Injection Molded |
| 3 . | Extruded Film |
| 4 . | Injection Molded |
| 5 . | Injection Molded |
| 6 . | Injection Molded |
| 7 . | Injection Molded |
| 8 . | Injection Molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 TFE 20 FR | RTP Company | Nylon 66 | RTP |
| YUNCON® N90 | YunNan YunTianHua Co., Ltd. | Acetal (POM) Copolymer | YUNCON® |
| YUNGSOX® PP 3015 | Formosa Polypropylene | PP Impact Copolymer | YUNGSOX® PP |
| Petrothene® GA605 | LyondellBasell Industries | LLDPE | Petrothene® |
| TOTAL Polypropylene PPC 4740WZ | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |