Nivionplast® B R50G NERO

Category: Nylon 6 , Polyamide 6
Manufacturer: SO.F.TER. SPA
Trademark: Nivionplast® B
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: pLXz5m_Nivionplast-B-R50G-NERO.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
50% glass fiber reinforced polyamide 6
General Information
Filler / Reinforcement
  • Glass Fiber, 50% Filler by Weight
Agency Ratings
  • EC 1907/2006 (REACH)
Appearance
  • Black
Processing Method
  • Injection Molding
PhysicalNominal ValueUnitTest Method
Specific Gravity 1.56g/cm³ASTM D792
Molding Shrinkage 0.15%Internal Method
Ash Content 50%Internal Method
MechanicalNominal ValueUnitTest Method
Tensile Modulus 15000MPaASTM D638
Tensile Strength (Break)190MPaASTM D638
Tensile Elongation (Break)3.0%ASTM D638
Flexural Modulus 15000MPaASTM D790
Flexural Strength 320MPaASTM D790
ImpactNominal ValueUnitTest Method
Notched Izod Impact (23°C)160J/mASTM D256
ThermalNominal ValueUnitTest Method
Deflection Temperature Under Load ASTM D648
    0.45 MPa, Unannealed 218°C
    1.8 MPa, Unannealed 208°C
Peak Melting Temperature 220°CASTM D3417
CLTE - Flow 2.5E-5cm/cm/°CASTM D696
FlammabilityNominal ValueTest Method
Flame Rating (3.20 mm)HBUL 94
InjectionNominal ValueUnit
Drying Temperature 90.0°C
Drying Time 4.0hr
Rear Temperature 250°C
Middle Temperature 270°C
Front Temperature 280°C
Mold Temperature 80.0 to 90.0°C
Resin Grade Manufacturer Category Trademark
Maxxam™ PP5120R B2 PolyOne Corporation PP Homopolymer Maxxam™
Sindustris PP H7412 Sincerity Australia Pty Ltd. PP, Unspecified Sindustris PP
ARMAMID® PA HC 20-1AF Poly Plastic Nylon 6 ARMAMID®
LEXAN™ HF1130R resin SABIC Innovative Plastics Europe PC LEXAN™
SABIC® PP PCGR40L Saudi Basic Industries Corporation (SABIC) PP Random Copolymer SABIC® PP