| HEAT STABILIZED,25% GLASS-FIBERS REINFORCED POLYAMIDE 6.6 FOR INJECTION MOULDING APPLICATIONS |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.40 - 0.50 | % | ASTM D955 |
| -- | 0.40 - 0.50 | % | ISO 2577 |
| Water Absorption | |||
| Saturation | 6.0 | % | ASTM D570 |
| Saturated, 23°C | 6.0 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.9 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 140 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 2.5 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 7200 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 200 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 70 | J/m | ASTM D256 |
| 23°C | 7.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 250 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, not annealed | 250 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 256 | °C | ISO 11357-3, ASTM D3417 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
| Dielectric Strength | 90 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.50 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 270 - 280 | °C | |
| Middle Temperature | 280 - 300 | °C | |
| Front Temperature | 285 - 310 | °C | |
| Mold Temperature | 65.0 - 110 | °C | |
| Injection Pressure | 70.0 - 125 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 35.0 - 85.0 | MPa | |
| Back Pressure | 0.350 - 0.700 | MPa | |
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Fill Speed: 50 to 75 mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Borealis PP BE170MO | Borealis AG | PP Copolymer | Borealis PP |
| HIVOREX J2200 | Lotte Chemical Corporation | HDPE | HIVOREX |
| Koylene SS35N | Reliance Industries Limited | PP Homopolymer | Koylene |
| LNP™ LUBRICOMP™ CX94108 compound | SABIC Innovative Plastics Europe | PS (HIPS) | LNP™ LUBRICOMP™ |
| POLYfill PPH GF5020 PB | Polykemi AB | PP Homopolymer | POLYfill |