Sindustris PBT HV1011
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pIelnh_Sindustris-PBT-HV1011.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sindustris PBT HV1011 is a Polybutylene Terephthalate (PBT) material. It is available in Asia Pacific for injection molding. Primary attribute of Sindustris PBT HV1011: Flame Rated. Typical application of Sindustris PBT HV1011: Electrical/Electronic Applications |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.2 to 2.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 53.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | > 100 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2260 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 83.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 34 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 57.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 154 | °C | |
| Peak Melting Temperature | 225 | °C | ASTM D3418 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI Str | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+19 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C, 1.00 mm) | 23 | kV/mm | ASTM D149 |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.810 mm | HB | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 230 to 235 | °C | |
| Middle Temperature | 235 to 245 | °C | |
| Front Temperature | 235 to 245 | °C | |
| Nozzle Temperature | 240 to 250 | °C | |
| Processing (Melt) Temp | 240 to 250 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ALCOM® PA6 900/8.4 GF10 MR20 | ALBIS PLASTIC GmbH | Nylon 6 | ALCOM® PA6 |
| Karina IVORY PVC COMPOUND MICRO-EX 4635/1-EXPO (**) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Hylon® N7233HL | Ravago Manufacturing Americas, LLC | Nylon 6/12 | Hylon® |
| LNP™ THERMOCOMP™ DF002 compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |
| OTECH ALLOY OM6018-Boot | OTECH Corporation | TP, Unspecified | OTECH ALLOY |