ALCOM® PC 740/4.19 WT1302-05LB
| Category: | PC , Polycarbonate |
| Manufacturer: | ALBIS PLASTIC GmbH |
| Trademark: | ALCOM® PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pIMNgN_ALCOMPC740419WT130205LB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALCOM®PC 740/4.19 WT1302-05LB is a polycarbonate (PC) product that contains fillers. It can be processed by injection molding and is available in North America, Europe or the Asia-Pacific region. ALCOM®The application fields of PC 740/4.19 WT1302-05LB include reflector, automobile industry and lighting equipment. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.33 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 36.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 130 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2700 | MPa | ISO 527-2 |
| Tensile Stress | 59.0 | MPa | ISO 527-2 |
| Flexural Modulus | 2840 | MPa | ISO 178 |
| Flexural Stress | 96.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 18 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 134 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 122 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 138 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 2.0 mm | 850 | °C | IEC 60695-2-12 |
| 3.0 mm | 850 | °C | IEC 60695-2-12 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tristimulus Value | |||
| Y10 of Reflection | 92 | % | DIN 5033 |
| Y10 of Transmission : 500.0 µm | 0.40 | % | ISO 13468 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 100 - 120 | °C | |
| Drying Time - Desiccant Dryer | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 310 - 330 | °C | |
| Mold Temperature | 80 - 130 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEPAZ™ LH40 | Mando Advanced Materials Co., Ltd. | PP Homopolymer | SEPAZ™ |
| Staramide AG5 | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| Karina CLEAR PVC COMPOUND -E 80/266-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| omay® SC42B | Suzhou OMAY Optical Materials Co., Ltd | Film, PP | omay® |
| Valtec HG619N | INDELPRO, S.A. de C.V. | PP Homopolymer | Valtec |