Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
Manufacturer: | Plastic Solutions, Inc. |
Trademark: | PrimaFlex® |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | pGqQ7s_PrimaFlex-CP-1804T.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
Description: CP 1804T is an easy flow injection molding impact copolymer polypropylene with 20% talc filled. |
General Information | |
---|---|
Filler / Reinforcement |
|
Features |
|
Uses |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 18 | g/10 min | ASTM D1238 |
Molding Shrinkage - Flow | 1.2 | % | ASTM D955 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Strength (Yield) | 23.0 | MPa | ASTM D638 |
Tensile Elongation (Break) | 150 | % | ASTM D638 |
Flexural Modulus | 2350 | MPa | ASTM D790 |
Flexural Strength | 40.0 | MPa | ASTM D790 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Notched Izod Impact | 190 | J/m | ASTM D256 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Deflection Temperature Under Load (1.8 MPa, Unannealed) | 65.0 | °C | ASTM D648 |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
NANCAR® 3245C | Nantex Industry Co., Ltd. | NBR | NANCAR® |
Dyna-Purge® K | Dyna-Purge, division of Shuman Plastics | Proprietary | Dyna-Purge® |
Hifax TYC 773P | LyondellBasell Industries | TPO (POE) | Hifax |
Infino LF-1025 | SAMSUNG SDI CO., LTD. | PC | Infino |
Domamid XS™ 5750R60H2 | Technical Polymers, LLC | Nylon 66 Alloy | Domamid XS™ |