LEXAN™ ML7672 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pGlCfX_LEXAN-ML7672-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Non FR PC + GF, UV-Stabilizer, balanced flow & impact. Available in Opaque only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 4.5 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 5.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.60 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.20 | % | |
| Equilibrium, 23°C, 50% RH | 0.30 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 5200 | MPa | ASTM D638 |
| -- | 5630 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield | 11.0 | MPa | ISO 527-2/5 |
| Break 2 | 52.0 | MPa | ASTM D638 |
| Break | 57.0 | MPa | ISO 527-2/5 |
| Tensile Strain | |||
| Yield | 0.30 | % | ISO 527-2/5 |
| Break 3 | 5.0 | % | ASTM D638 |
| Break | 1.8 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 4860 | MPa | ASTM D790 |
| -- 5 | 5480 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 100 | MPa | ISO 178 |
| Yield, 50.0 mm Span 6 | 99.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 7(23°C) | 19 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C | 240 | J/m | ASTM D256 |
| 23°C 8 | 19 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 28.2 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 138 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 9 | 140 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 143 | °C | ASTM D1525, ISO 306/B50 11 10 |
| -- | 145 | °C | ISO 306/B120 |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 2.7E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.9E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 293 to 316 | °C | |
| Middle Temperature | 304 to 327 | °C | |
| Front Temperature | 316 to 338 | °C | |
| Nozzle Temperature | 310 to 332 | °C | |
| Processing (Melt) Temp | 316 to 338 | °C | |
| Mold Temperature | 82.2 to 116 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 sp=62mm |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 104 HB | RTP Company | PP, Unspecified | RTP |
| WPP PP JOSB26286-Black | Washington Penn Plastic Co. Inc. | PP Impact Copolymer | WPP PP |
| Armlen® PP SC 15-2 (C) | Poly Plastic | PP, Unspecified | Armlen® |
| AVP™ GLC08CP | SABIC Innovative Plastics | PC+ABS | AVP™ |
| HiFill® PA6 GF50 LE | Techmer Engineered Solutions | Nylon 6 | HiFill® |