VITAMIDE® AR76NT6585
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | VITAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pGgSS0_VITAMIDE-AR76NT6585.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VITAMIDE® AR76NT6585 is a Polyamide 66 (Nylon 66) product filled with 30% glass fiber. It is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792, ISO 1183 |
| Water Absorption (23°C, 24 hr) | 0.80 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 180 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 8200 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 255 | MPa | ISO 178 |
| Break | 255 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 11 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 45 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength | 11 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 240 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 235 | °C | ASTM D648, ISO 75-2/A |
| Peak Melting Temperature | 258 | °C | ASTM D2117, ISO 1218 |
| CLTE - Flow | 2.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | 28 | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Oxygen Index | 23 | % | ASTM D2863, ISO 4589-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Scolefin 53 G 10-0 | Ravago Group | PP Homopolymer | Scolefin |
| Staramide AG6K | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| Edistir® RT 461F | Versalis S.p.A. | PS (HIPS) | Edistir® |
| Hostacom M4 U04 100000 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| PLUSTEK PB300G5 | Polyram Ram-On Industries | Nylon 6 | PLUSTEK |