VITAMIDE® AS10GR6664
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | VITAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pGGGRm_VITAMIDE-AS10GR6664.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VITAMIDE® AS10GR6664 is a Polyamide 66 (Nylon 66) product. It is available in Europe. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (275°C/0.325 kg) | 7.0 | g/10 min | ISO 1133 |
| Water Absorption | |||
| 24 hr | 1.8 | % | ASTM D570 |
| 23°C, 24 hr | 1.8 | % | ISO 62 |
| Saturation | 8.0 | % | ASTM D570 |
| Saturation, 23°C | 8.0 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 80.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 9.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2800 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 105 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 38 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 200 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 70.0 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 260 | °C | ISO 1218, ASTM D2117 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257, IEC 60093 |
| Dielectric Strength | 27 | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index | |||
| Solution A | > 600 | V | IEC 60112 |
| -- 1 | > 600 | V | ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-2 | UL 94 | |
| Oxygen Index | 26 | % | ASTM D2863, ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Solution A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIDILENA III HDPE RBF0.08 | ROMPETROL PETROCHEMICALS S.R.L. | HDPE | MIDILENA III |
| Sindustris PBT SG5151 | Sincerity Australia Pty Ltd. | PBT+PET | Sindustris PBT |
| YUPLENE® H220P | SK Global Chemical | PP Homopolymer | YUPLENE® |
| Hostaform® XGC25-LW01 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| LG EVA EC33018 | LG Chem Ltd. | EVA | LG EVA |