Bakelite® PF 2560
| Category: | Phenolic , Phenolic |
| Manufacturer: | Hexion Inc. |
| Trademark: | Bakelite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pF2Yg8_Bakelite-PF-2560.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product Description Phenolic moulding compound, inorganically/organically filled, average heat resistance, high surface quality, lower water absorption than PF 31, minimal distortion, UL listed moulding compound 1.5 mm / V-1 (ALL), 3.0 mm / V-0 (ALL) Application Areas Housings for domestic appliances, oven strips |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.59 | g/cm³ | ISO 1183 |
| Apparent Density | 0.75 | g/cm³ | ISO 60 |
| Molding Shrinkage 1 | 0.75 | % | ISO 2577 |
| Water Absorption - 24h/23C | 20.0 | mg | ISO 62 |
| Post Shrinkage 2 | 0.40 | % | ISO 2577 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Molding Pressure | > 15.0 | MPa | |
| Compression Molding Temperature | 160 to 190 | °C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 350 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9000 | MPa | ISO 527-2/1 |
| Tensile Stress | 50.0 | MPa | ISO 527-2/5 |
| Flexural Modulus | 9000 | MPa | ISO 178 |
| Flexural Stress 3 | 90.0 | MPa | ISO 178 |
| Compressive Stress | 250 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.6 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (8.0 MPa, Unannealed) | 115 | °C | ISO 75-2/C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+11 | ohms·cm | IEC 60093 |
| Electric Strength 4(1.00 mm) | 6.0 | kV/mm | IEC 60243-1 |
| Relative Permittivity (100 Hz) | 14.5 | IEC 60250 | |
| Dissipation Factor (100 Hz) | 0.20 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 125 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm, All | V-1 | ||
| 1.50 mm, Black, Natural | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 60.0 to 75.0 | °C | |
| Nozzle Temperature | 80.0 to 100 | °C | |
| Processing (Melt) Temp | 80.0 to 100 | °C | |
| Mold Temperature | 160 to 190 | °C | |
| Injection Pressure | > 15.0 | MPa | |
| Back Pressure | 0.500 to 2.00 | MPa |
| Note Message | |
|---|---|
| 1 . | Injection |
| 2 . | Injection |
| 3 . | 2.0 mm/min |
| 4 . | short term, electrode layout P25mm/P25mm in transformer oil equivalent to IEC 60296 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| McCann PP M10TCPP10 | McCann Plastics Inc. | PP Copolymer | McCann PP |
| NOVADURAN® 5308F20 | Mitsubishi Engineering-Plastics Corp | PBT Alloy | NOVADURAN® |
| Flontech® FT-BRR40-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Hanwha Total PP GH42M | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| LEMALLOY® BX504D | Mitsubishi Engineering-Plastics Corp | PPE+Nylon 6 | LEMALLOY® |