SCHULADUR® A GF 15 HI
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULADUR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pEMG9E_SCHULADUR-A-GF-15-HI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 15% glass fibre reinforced and impact modified PBT-grade |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 15.0 | cm³/10min | ISO 1133 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5200 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 92.5 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.8 | % | ISO 527-2/1A/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 6.0 | kJ/m² | ISO 179/1eA |
| 23°C | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 33 | kJ/m² | ISO 179/1eU |
| 23°C | 61 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 217 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 190 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 219 | °C | ISO 306/A50 |
| -- | 197 | °C | ISO 306/B50 |
| Ball Pressure Test (200°C) | Pass | IEC 60695-10-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 375 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 1.60 mm | HB | IEC 60695-11-10, -20 | |
| 3.20 mm | HB | IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.50 mm | 725 | °C | IEC 60695-2-12 |
| 3.00 mm | 725 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.50 mm | 750 | °C | IEC 60695-2-13 |
| 3.00 mm | 750 | °C | IEC 60695-2-13 |
| Oxygen Index | 19 | % | ISO 4589-2 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Qenos PP PPK 1060 | Qenos Pty Ltd | PP Homopolymer | Qenos PP |
| Altuglas® V 045 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Altuglas® |
| EVAL™ LR171B | EVAL Europe nv | EVOH | EVAL™ |
| Sylvin 9604-80 Purple 8460 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ THERMOCOMP™ DB008ERP compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |