POCAN® BFN 4211 000000 000000
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | LANXESS Asia/Pacific |
| Trademark: | POCAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pEDX3G_POCAN-BFN-4211-000000-000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT, 13 % glass fibers, injection molding, halogen free flame retardant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.43 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 2577 | ||
| Across Flow : 260°C, 2.00 mm 1 | 1.1 | % | |
| Across Flow : 120°C, 4 hr, 2.00 mm 2 | 0.10 | % | |
| Flow : 260°C, 2.00 mm 3 | 0.60 | % | |
| Flow : 120°C, 4 hr, 2.00 mm 4 | 0.10 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 6200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 75.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.7 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 6700 | MPa | ISO 178/A |
| Flexural Stress 6(23°C) | 125 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 2.7 | % | ISO 178/A |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PBT, GFHMR, 09-060, GF13 | ISO 7792 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.0 to 0.020 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | < 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 25 | kJ/m² | |
| 23°C | 30 | kJ/m² | |
| Notched Izod Impact Strength (23°C) | < 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 23 | kJ/m² | |
| 23°C | 25 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 190 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 206 | °C | ISO 306/B50 |
| Ball Pressure Test (215°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature 8 | 220 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 4.0E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 9.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 6.6E+15 | ohms·cm | IEC 60093 |
| Electric Strength (23°C, 1.00 mm) | 33 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.400 mm | V-0 | ||
| 0.750 mm | V-0 | ||
| 1.50 mm | V-0 5VA | ||
| 3.00 mm | V-0 5VA | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.400 mm | 960 | °C | |
| 0.750 mm | 960 | °C | |
| 1.50 mm | 960 | °C | |
| 3.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.400 mm | 775 | °C | |
| 0.750 mm | 775 | °C | |
| 1.50 mm | 775 | °C | |
| 3.00 mm | 775 | °C |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Circulation Dryer | 120 | °C | |
| Drying Time - Circulation Dryer | 4.0 to 8.0 | hr | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPE ME-2640DB BLK (PRELIMINARY DATA) | Teknor Apex Company | TPE | Sarlink® TPE |
| ADENE BFFBL | A.D. Compound spa | PP Homopolymer | ADENE |
| ICORENE® 1869 | ICO Polymers EMEA, A Division of A. Schulman | LLDPE | ICORENE® |
| LG PVC LS100E | LG Chem Ltd. | PVC Homopolymer | LG PVC |
| Rotuba CAP CP801 (10% Plasticizer) | Rotuba Extruders, Inc. | CAP | Rotuba CAP |