LNP™ LUBRICOMP™ RP003 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pE8iYS_LNP-LUBRICOMP-RP003-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP RP003 is a compound based on Nylon 66 resin containing 15% PTFE/Silicone. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound RL-4530 Product reorder name: RP003 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Across Flow : 24 hr | 1.0 to 3.0 | % | ASTM D955 |
| Flow : 24 hr | 1.0 to 3.0 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.60 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.97 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2690 | MPa | ASTM D638 |
| -- | 2960 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 52.0 | MPa | ASTM D638 |
| Yield | 55.0 | MPa | ISO 527-2/5 |
| Break 3 | 49.0 | MPa | ASTM D638 |
| Break | 55.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 4.6 | % | ASTM D638 |
| Yield | 4.8 | % | ISO 527-2/5 |
| Break 5 | 4.7 | % | ASTM D638 |
| Break | 4.7 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2260 | MPa | ASTM D790 |
| -- 7 | 2590 | MPa | ISO 178 |
| Flexural Strength 8 | ASTM D790 | ||
| Yield, 50.0 mm Span | 73.4 | MPa | |
| Break, 50.0 mm Span | 73.4 | MPa | |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.23 | ||
| vs. Itself - Static | 0.17 | ||
| Wear Factor - Washer | 10.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 37 | J/m | ASTM D256 |
| 23°C 9 | 4.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 380 | J/m | ASTM D4812 |
| 23°C 10 | 26 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 1.40 | J | ASTM D3763 |
| -- | 0.900 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 201 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 11 | 221 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 59.4 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 66.0 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 9.0E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 9.1E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 9.5E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 9.6E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 277 to 288 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime ABS ST80 | Primex Plastics Corporation | ASA+ABS | Prime ABS |
| Pyramid™ PPS SE2219 | Polymics, Ltd. | PPS | Pyramid™ PPS |
| TECHNYL® B 738 MX15 BLACK 61 | Solvay Engineering Plastics | Nylon 66/6 | TECHNYL® B |
| ALCUDIA® LDPE 2625FG | REPSOL | LDPE | ALCUDIA® LDPE |
| Borealis PP BC545MO | Borealis AG | PP Impact Copolymer | Borealis PP |