Pro-fax 7523
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Pro-fax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pDvrDF_Pro-fax-7523.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Pro-fax 7523 impact polypropylene copolymer is available in pellet form. This resin is typically used in injection molding applications and offers good cold temperature impact resistance. An ASTM and ISO-based versions of the technical datasheet are available for Pro-fax 7523 For regulatory compliance information see Pro-fax 7523 Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.898 | g/cm³ | ASTM D792B |
| -- | 0.900 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 28.0 | MPa | ASTM D638 |
| Yield, 23°C | 26.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 9.0 | % | ASTM D638 |
| Yield, 23°C | 9.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| 1% Secant 2 | 1240 | MPa | ASTM D790A |
| 23°C | 1220 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40°C | 2.5 | kJ/m² | |
| 23°C | 10 | kJ/m² | |
| Notched Izod Impact | |||
| 23°C | 85 | J/m | ASTM D256A |
| 23°C | 9.9 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 82.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 76.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 49.0 | °C | ISO 75-2/A |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PTS POM-90 | Polymer Technology and Services, LLC | Acetal (POM) Copolymer | PTS |
| TAIRILAC AG15E1 | Formosa Plastics Corporation | ABS | TAIRILAC |
| Vikalloy P45 | Viking Polymers, LLC | CPVC | Vikalloy |
| XYRON™ 400H | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| LNP™ LUBRICOMP™ UCL36S compound | SABIC Innovative Plastics | PPA | LNP™ LUBRICOMP™ |