MAJORIS EE265 GRIS 8683/FZH
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pDGGdk_MAJORIS-EE265-GRIS-8683-FZH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EE 265 GRIS 8683/FZH is a 25% mineral filled polypropylene elastomer modified compound intended for injection moulding. EE 265 GRIS 8683/FZH has been developed especially for the automotive interior parts, requiring good impact strength/stiffness, very good scratch resistance and UV resistance. The product is available in natural (EE 265) and black (EE 265-8229) but other colours can be provided on request. APPLICATIONS Automotive interior parts |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.10 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.80 - 1.1 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 21.0 | MPa | ISO 527-2/50 |
| Flexural Modulus 1 | 2200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1A | ||
| 0°C | 5.0 | kJ/m² | ISO 179/1A |
| 23°C | 14 | kJ/m² | ISO 179/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 110 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 60.0 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULINK® XL 350-S | A. Schulman Inc. | XLPE | SCHULINK® |
| AKROMID® B3 GF 25 1 L natural (4781) | AKRO-PLASTIC GmbH | Nylon 6+PP | AKROMID® |
| Delta N66R-4G40 | Delta Polymers | Nylon 66 | Delta |
| Karina BLACK PVC COMPOUND 750-DM-48/1-B-IS (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PLUSTEK PB320G3 | Polyram Ram-On Industries | Nylon 6 | PLUSTEK |