Plenco 04301 (Injection)
| Category: | Phenolic , Phenolic |
| Manufacturer: | Plastics Engineering Co. |
| Trademark: | Plenco |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pCkNMh_Plenco-04301-Injection-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PLENCO 04301 is a heat resistant, mineral filled phenolic molding compound offering excellent dimensional stability and electrical properties. UL recognized under component file E40654. 04301 is available in black. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792 |
| Apparent Density | 0.62 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 0.74 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.19 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 80 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8710 | MPa | ASTM D638 |
| Tensile Strength | 50.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.70 | % | ASTM D638 |
| Flexural Modulus | 7860 | MPa | ASTM D790 |
| Flexural Strength | 79.9 | MPa | ASTM D790 |
| Compressive Strength | 184 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 15.3 | J/m | ASTM D256 |
| Notched Izod Impact | 14 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 173 | °C | ASTM D648 |
| Continuous Use Temperature | 201 | °C | ASTM D794 |
| CLTE - Flow | 4.4E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.7E+11 | ohms·cm | ASTM D257 |
| Dielectric Strength | ASTM D149 | ||
| -- 1 | 11 | kV/mm | ASTM D149 |
| -- 2 | 7.2 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 5.50 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.064 | ASTM D150 | |
| Arc Resistance | 163 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 175 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 | |
| Oxygen Index | 40 | % | ASTM D2863 |
| Additional Information |
|---|
| The value listed as Mold Shrink, Linear-Flow, ASTM D955 was tested according to the ASTM D6289 standard.The value listed as Comparative Tracking Index, UL 746 was tested according to ASTM D3638.Post Shrinkage, ASTM D6289, 72hr, 120°C: 0.23%Heat Resistance, ASTM D794: 201°CDrop Ball Impact, PLENCO Method: 82 J/m |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Shot Size | 20 - 80 | % | |
| Rear Temperature | 66.0 - 82.0 | °C | |
| Front Temperature | 82.0 - 99.0 | °C | |
| Processing (Melt) Temp | 104 - 115 | °C | |
| Mold Temperature | 165 - 182 | °C | |
| Injection Pressure | 6.20 - 11.0 | MPa | |
| Back Pressure | 0.300 | MPa | |
| Screw Speed | < 60 | rpm | |
| Cushion | 3.00 | mm |
| Injection instructions |
|---|
| Injection Time: 3-8 sec |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| 2 . | Method B (step by step) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P1765B | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Ravago Compounds HM-267 | Ravago Manufacturing Americas, LLC | LLDPE | Ravago Compounds |
| REVOLVE® M-776 | Matrix Polymers | PE, Unspecified | REVOLVE® |
| VisiJet® M3 Techplast | 3D Systems | Unspecified | VisiJet® |
| Vynaprene 7907 | Axiall Corporation | PVC, Rigid | Vynaprene |