TEKASTER™ F101FR

Category: PBT , Polybutylene Terephthalate
Manufacturer: Mando Advanced Materials Co., Ltd.
Trademark: TEKASTER™
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: pCXdCL_TEKASTER-F101FR.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
TEKASTER™ F101FR is a Polybutylene Terephthalate (PBT) product. It is available in Asia Pacific. Primary characteristic: flame retardant.
General Information
Features
  • Flame Retardant
PhysicalNominal ValueUnitTest Method
Specific Gravity 1.42g/cm³ASTM D792
Molding Shrinkage - Flow 11.6%ASTM D955
MechanicalNominal ValueUnitTest Method
Tensile Strength 58.8MPaASTM D638
Tensile Elongation (Break)20%ASTM D638
Flexural Modulus 2750MPaASTM D790
Flexural Strength 103MPaASTM D790
ImpactNominal ValueUnitTest Method
Notched Izod Impact 34J/mASTM D256
ThermalNominal ValueUnitTest Method
Deflection Temperature Under Load ASTM D648
    0.45 MPa, Unannealed 168°C
    1.8 MPa, Unannealed 70.0°C
InjectionNominal ValueUnit
Drying Temperature 110 to 130°C
Drying Time 3.0 to 5.0hr
Rear Temperature 230 to 270°C
Middle Temperature 210 to 260°C
Front Temperature 200 to 250°C
Nozzle Temperature 230 to 270°C
Processing (Melt) Temp 230 to 250°C
Mold Temperature 40.0 to 60.0°C
Injection Pressure 39.2 to 132MPa
Note Message
1 .60°C Mold Temperature
Resin Grade Manufacturer Category Trademark
Stirofor® HI-V2 NATURALE SO.F.TER. SPA PS (HIPS) Stirofor®
Stratasys PC-ISO Stratasys PC Stratasys
Therma-Tech™ X TT9200-8706 EC PolyOne Corporation PPS Therma-Tech™
Epiall® 1908B-1 Sumitomo Bakelite North America, Inc. Epoxy Epiall®
LNP™ VERTON™ MV008S compound SABIC Innovative Plastics PP, Unspecified LNP™ VERTON™