LNP™ LUBRICOMP™ UFL36AS compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pAv4FO_LNP-LUBRICOMP-UFL36AS-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP UFL36AS is a Polyphthalamide (PPA) base resin containing 30% Glass Fiber, 15% PTFE. Added features of this material are: Heat Stabilized, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound UFL-4036 A HS Product reorder name: UFL36AS |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.58 | g/cm³ | ASTM D792 |
| -- | 1.57 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.20 to 0.40 | % | |
| Across Flow : 24 hr | 0.80 to 1.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.15 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.25 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 15400 | MPa | ASTM D638 |
| -- 2 | 15400 | MPa | ASTM D638 |
| -- | 12600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 189 | MPa | ASTM D638 |
| Yield | 192 | MPa | ISO 527-2/5 |
| Break 4 | 189 | MPa | ASTM D638 |
| Break | 192 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 5 | 1.8 | % | ASTM D638 |
| Yield | 2.0 | % | ISO 527-2/5 |
| Break 6 | 1.7 | % | ASTM D638 |
| Break | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 7 | 10600 | MPa | ASTM D790 |
| -- 8 | 11300 | MPa | ISO 178 |
| Flexural Strength 9 | ASTM D790 | ||
| Yield, 50.0 mm Span | 242 | MPa | |
| Break, 50.0 mm Span | 233 | MPa | |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.48 | ||
| vs. Itself - Static | 0.52 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 0.100 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 5.00 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 95 | J/m | ASTM D256 |
| 23°C 10 | 9.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 710 | J/m | ASTM D4812 |
| 23°C 11 | 47 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 8.90 | J | ASTM D3763 |
| -- | 2.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 277 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 273 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 2.1E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 4.5E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 310 to 321 | °C | |
| Middle Temperature | 316 to 327 | °C | |
| Front Temperature | 327 to 338 | °C | |
| Processing (Melt) Temp | 316 to 332 | °C | |
| Mold Temperature | 149 to 171 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | Type I, 5.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Acrigel® LEP100 | Unigel Plásticos | Acrylic (PMMA) | Acrigel® |
| FM® 50 | Cytec Industries Inc. | PI, TS | FM® |
| Hostaform® C 9021 K | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Karina IVORY PVC COMPOUND -E 858-35/ 1-DY-IS-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Moplen EP640T | PolyMirae | PP Impact Copolymer | Moplen |