ELITE™ 5401G
| Category: | EPE , Enhanced Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ELITE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | p9ttGk_ELITE-5401G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
ELITE™ 5401G Enhanced Polyethylene Resin is a copolymer produced via INSITE™ Technology from Dow. It offers a unique combination of low seal initiation, moderate stiffness and low blocking for excellent performance on automated packaging equipment.
Complies with:
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Puncture Energy | 1.69 | J | Internal method |
| Film Puncture Force | 35.6 | N | Internal method |
| Film Puncture Resistance | 9.10 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD | 70.3 | J/cm³ | ASTM D882 |
| TD | 66.2 | J/cm³ | ASTM D882 |
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 179 | MPa | ASTM D882 |
| 2% secant, MD | 159 | MPa | ASTM D882 |
| 1% secant, TD | 200 | MPa | ASTM D882 |
| 2% secant, TD | 165 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 11.7 | MPa | ASTM D882 |
| TD : Yield | 11.0 | MPa | ASTM D882 |
| MD : Fracture | 33.8 | MPa | ASTM D882 |
| TD : Fracture | 27.6 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 400 | % | ASTM D882 |
| TD : Fracture | 450 | % | ASTM D882 |
| Dart Drop Impact | 450 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 250 | g | ASTM D1922 |
| TD | 550 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 100 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 123 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 33 | ASTM D2457 | |
| Haze | 22 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：3.5 英寸 螺杆类: DSB II 模具间隙：70 密尔 (1.8 mm) 熔体温度： 410°F 输出：模具周长的 12 磅/小时/英寸 模具直径：8 英寸 放大比：2.5:1 螺杆速度：40 rpm 冷冻线高度：47 in. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RIGITRON 20415 GF | Ovation Polymers Inc. | PBT | RIGITRON |
| CP PRYME® Polycarbonate PC300HFR | Chase Plastics Services Inc. | PC | CP PRYME® Polycarbonate |
| elitel UE3660 | UNITIKA Plastics Division | TPC-ET | elitel |
| Grivory® GV-5H | EMS-GRIVORY | Nylon 66+Nylon 6I/X | Grivory® |
| LUVOCOM® 3-8097 VP | Lehmann & Voss & Co. | Nylon 6 | LUVOCOM® |