SABIC® PP 108MF10
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | p9mtbN_SABIC-PP-108MF10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PP 108MF10 is a super high impact copolymer which exhibits an unmatched cold impact resistance, high flow and excellent paint adhesion characteristics. Because of this unique and well balanced property profile our customers commonly use this material for painted car bumpers. SABIC® PP 108MF10 is a designated automotive grade. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow : 24 hr | 1.5 | % | |
| 24 hr | 1.5 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Injection Molded) | 52 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 1% Secant : Injection Molded 1 | 1000 | MPa | ASTM D638 |
| Injection Molded | 1000 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield, Injection Molded 2 | 19.0 | MPa | ASTM D638 |
| Yield, Injection Molded | 19.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield, Injection Molded 3 | 8.0 | % | ASTM D638 |
| Yield, Injection Molded | 8.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| 0°C, Injection Molded | No Break | ||
| 23°C, Injection Molded | No Break | ||
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact | |||
| -20°C, Injection Molded | No Break | ASTM D256A | |
| 0°C, Injection Molded | No Break | ASTM D256A, ISO 180/1A | |
| 23°C, Injection Molded | No Break | ASTM D256A, ISO 180/1A | |
| -20°C, Injection Molded | 35 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 130 | °C | ASTM D1525, ISO 306/A120 5 4 |
| -- | 50.0 | °C | ASTM D1525, ISO 306/B120 6 5 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | Rate B (120°C/h), Loading 1 (10 N) |
| 5 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ NatureGran PO1000 | TER HELL PLASTIC GMBH | PLA | TEREZ NatureGran |
| Nypol® PA A3 AZL0039 NR318 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| DJSilicone NE-8135 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Gravi-Tech™ GRV-NY-050-CU-NAT | PolyOne Corporation | Nylon 6 | Gravi-Tech™ |
| HiFill® PA6/6 GF/M38 HS | Techmer Engineered Solutions | Nylon 66 | HiFill® |