LNP™ THERMOTUF™ R1000I compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOTUF™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | p8bcUx_LNP-THERMOTUF-R1000I-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOTUF R1000I is a compound based on Nylon 66 resin containing Impact Modifier. Added feature of this material is: High Impact. Also known as: LNP* THERMOTUF* Compound R-1000 HI Product reorder name: R1000I |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.09 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (24 hr) | 1.1 to 1.5 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 45.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 70 | % | ISO 527-2 |
| Flexural Modulus | 1400 | MPa | ISO 178 |
| Flexural Stress | 50.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 1(23°C) | 55 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 2(23°C) | 98 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed, 64.0 mm Span) | 65.0 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 254 to 266 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 266 to 277 | °C | |
| Mold Temperature | 60.0 to 98.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3671A NAT 601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Sinpolene MBW1791 | Teknor Apex Asia Pacific PTE. LTD. | LLDPE | Sinpolene |
| Aplax P2813GN | Ginar Technology Co., LTD. | PP, Unspecified | Aplax |
| Elvax® 3170 | DuPont Packaging & Industrial Polymers | EVA | Elvax® |
| Iupiace® TX903B | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |