PRL TP-GFMF1
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | p8EGqs_PRL-TP-GFMF1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL TP-GFMF1 is a Polybutylene Terephthalate (PBT) product filled with 40% glass\mineral. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.75 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 2.0 to 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.40 to 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 96.5 | MPa | |
| Break, 3.18 mm | 96.5 | MPa | |
| Flexural Modulus (3.18 mm) | 10000 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 159 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 204 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 188 | °C | |
| RTI Elec (1.50 mm) | 75.0 | °C | UL 746 |
| RTI Imp (1.50 mm) | 75.0 | °C | UL 746 |
| RTI Str (1.50 mm) | 75.0 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| High Amp Arc Ignition (HAI) (1.50 mm) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) (1.50 mm) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 116 to 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 243 to 254 | °C | |
| Middle Temperature | 249 to 260 | °C | |
| Front Temperature | 254 to 266 | °C | |
| Processing (Melt) Temp | 249 to 277 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP PCGR25 | Saudi Basic Industries Corporation (SABIC) | PP Random Copolymer | SABIC® PP |
| ALCOM® PA46 920/1 PTFE15 | ALBIS PLASTIC GmbH | Nylon 46 | ALCOM® PA46 |
| ASACOM™ S9500-10 | Polymer Compounders Limited | ASA | ASACOM™ |
| Hostalen H5416K | LyondellBasell Industries | PP Random Copolymer | Hostalen |
| Stat-Tech™ PA66 C20 black (EM00000364BI) | PolyOne Corporation | Nylon 66 | Stat-Tech™ |