CYCOLAC™ MG94 resin

Category:	ABS , Acrylonitrile Butadiene Styrene
Manufacturer:	SABIC Innovative Plastics
Trademark:	CYCOLAC™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	p887SN_CYCOLAC-MG94-resin.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
Superior flow, injection molding ABS. Good impact. For thin-wall applications.

General Information
Features	Good Flow Good Impact Resistance
Uses	Thin-walled Parts
Processing Method	Injection Molding
Multi-Point Data	Coefficient of Thermal Expansion vs. Temperature (ASTM E831) Flexural DMA (ASTM D4065) Shear DMA (ASTM D4065) Specific Heat vs. Temperature (ASTM D3417) Tensile Creep (ASTM D2990) Tensile Fatigue Tensile Stress vs. Strain (ASTM D638) Thermal Conductivity vs. Temperature (ASTM E1530) Viscosity vs. Shear Rate (ASTM D3835)

Physical	Nominal Value	Unit	Test Method
Specific Gravity
--	1.05	g/cm³	ASTM D792
--	1.04	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR)
230°C/3.8 kg	12	g/10 min	ASTM D1238
220°C/10.0 kg	42	g/10 min	ISO 1133
220°C/5.0 kg	13	g/10 min	ISO 1133
Molding Shrinkage - Flow (3.20 mm)	0.50 to 0.80	%	Internal Method

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale)	113		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus
-- ¹	2480	MPa	ASTM D638
--	2450	MPa	ISO 527-2/1
Tensile Strength
Yield ²	46.0	MPa	ASTM D638
Yield	46.0	MPa	ISO 527-2/50
Break ³	35.0	MPa	ASTM D638
Break	35.0	MPa	ISO 527-2/50
Tensile Elongation
Yield ⁴	2.0	%	ASTM D638
Yield	2.3	%	ISO 527-2/50
Break ⁵	18	%	ASTM D638
Break	40	%	ISO 527-2/50
Flexural Modulus
50.0 mm Span ⁶	2620	MPa	ASTM D790
-- ⁷	2500	MPa	ISO 178
Flexural Stress
--	70.0	MPa	ISO 178
Yield, 50.0 mm Span ⁸	79.0	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength ⁹(23°C)	18	kJ/m²	ISO 179/1eA
Notched Izod Impact
-30°C	80	J/m	ASTM D256
23°C	240	J/m	ASTM D256
-30°C ¹⁰	7.0	kJ/m²	ISO 180/1A
23°C ¹¹	16	kJ/m²	ISO 180/1A
Instrumented Dart Impact			ASTM D3763
-30°C, Total Energy	5.00	J
23°C, Total Energy	21.0	J

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load
0.45 MPa, Unannealed, 3.20 mm	96.0	°C	ASTM D648
0.45 MPa, Unannealed, 100 mm Span ¹²	89.0	°C	ISO 75-2/Be
1.8 MPa, Unannealed, 3.20 mm	82.0	°C	ASTM D648
1.8 MPa, Unannealed, 100 mm Span ¹³	76.0	°C	ISO 75-2/Ae
Vicat Softening Temperature
--	98.0	°C	ASTM D1525, ISO 306/B50 11 ¹⁴
--	100	°C	ISO 306/B120
CLTE			ASTM E831, ISO 11359-2
Flow : -40 to 40°C	8.8E-5	cm/cm/°C
Transverse : -40 to 40°C	8.5E-5	cm/cm/°C
RTI Elec	60.0	°C	UL 746
RTI Imp	60.0	°C	UL 746
RTI Str	60.0	°C	UL 746

Flammability	Nominal Value		Test Method
Flame Rating (1.52 mm)	HB		UL 94

Fill Analysis	Nominal Value	Unit	Test Method
Melt Viscosity (240°C, 1000 sec^-1)	173	Pa·s	ASTM D3835

Injection	Nominal Value	Unit
Drying Temperature	82.2 to 87.8	°C
Drying Time	2.0 to 4.0	hr
Drying Time, Maximum	8.0	hr
Suggested Max Moisture	0.10	%
Suggested Shot Size	50 to 70	%
Rear Temperature	188 to 199	°C
Middle Temperature	199 to 210	°C
Front Temperature	204 to 227	°C
Nozzle Temperature	204 to 246	°C
Processing (Melt) Temp	204 to 246	°C
Mold Temperature	48.9 to 71.1	°C
Back Pressure	0.345 to 0.689	MPa
Screw Speed	30 to 60	rpm
Vent Depth	0.038 to 0.051	mm

Note Message
1 .	5.0 mm/min
2 .	Type I, 5.0 mm/min
3 .	Type I, 5.0 mm/min
4 .	Type I, 5.0 mm/min
5 .	Type I, 5.0 mm/min
6 .	1.3 mm/min
7 .	2.0 mm/min
8 .	1.3 mm/min
9 .	80104 sp=62mm
10 .	80104
11 .	80104
12 .	120104 mm
13 .	120104 mm
14 .	Rate B (120°C/h), Loading 2 (50 N)

Resin Grade	Manufacturer	Category	Trademark
SCHULAMID® 6 HV 11	A. Schulman Europe	Nylon 6	SCHULAMID®
Sinpolene MBW1391	Teknor Apex Asia Pacific PTE. LTD.	LLDPE	Sinpolene
Starex WR-9300HF	SAMSUNG SDI CO., LTD.	ASA	Starex
GAPEX® HPP30GR24HB BLACK	Ferro Corporation	PP Homopolymer	GAPEX®
Pinnacle PP 1120 Z	Pinnacle Polymers	PP Homopolymer	Pinnacle PP