Order Products : sales@su-jiao.com
LNP™ THERMOCOMP™ RF006S compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | p7zidw_LNPTHERMOCOMPRF006Scompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP RF006S is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound RF-1006 HS Product reorder name: RF006S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 10300 | MPa | ASTM D638 |
| Tensile Strength (Break) | 159 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 10300 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 248 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® COPP 17.NB | Marco Polo International, Inc. | PP Impact Copolymer | MARPOL® COPP |
| RTP 280.5 TFE 13 SI 2 | RTP Company | Nylon 66 | RTP |
| Taitalac® 1000 | Taita Chemical Company, Ltd. | ABS | Taitalac® |
| LUVOCOM® 20-7908 VP | Lehmann & Voss & Co. | PPA | LUVOCOM® |
| Sylvin 7011EE-90 BLACK | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |