Hyosung Polyketone M620A
| Category: | PK-Aliphatic , Polyketone, Aliphatic |
| Manufacturer: | Hyosung Corporation |
| Trademark: | Hyosung Polyketone |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | p7sYG2_Hyosung-Polyketone-M620A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hyosung Polyketone M620A A high viscosity grade for injection molding & extrusion. (Natural color) |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (240°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.8 to 2.0 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 60% RH) | 0.45 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 58.8 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | > 300 | % | ASTM D638 |
| Flexural Modulus (23°C) | 1470 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 58.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 118 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 200 | °C | |
| 1.8 MPa, Unannealed | 100 | °C | |
| Melting Temperature | 210 | °C | ASTM D1525 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 17 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DINAPLEN® PPH1S07 G40-4137 | Grupo Repol | PP Homopolymer | DINAPLEN® |
| Eltex® MED 100-MG12 | INEOS Olefins & Polymers Europe | PP Homopolymer | Eltex® MED |
| Hostaform® XGC25 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| OMIKRON BG 706 NERO | TECNOPOL | PP Homopolymer | OMIKRON |
| 3M™ Dyneon™ PTFE Compound NST 1111R | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |