Ultramid® 8254 HS BK-102
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | p7KiIw_Ultramid-8254-HS-BK-102.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid 8254 HS BK-102 is a highly flexible, heat stabilized, pigmented black, impact modified PA6 extrusion compound for tubing application. Applications Ultramid 8254 HS BK-102 is generally recommended for applications such as convoluted and emission tubing, cable jacketing and other types of automotive tubing. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.07 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (3.18 mm) | 1.3 | -- | % | |
| Water Absorption | ||||
| 24 hr | 1.2 | -- | % | ASTM D570 |
| 23°C, 24 hr | 1.2 | -- | % | ISO 62 |
| Saturation | 7.1 | -- | % | ASTM D570 |
| Saturated, 23°C | 7.1 | -- | % | ISO 62 |
| Balance, 50% RH | 2.0 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 2.0 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 40 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| -40°C | 2730 | 3000 | MPa | ISO 527-2 |
| 23°C | 875 | 460 | MPa | ISO 527-2 |
| 80°C | 180 | 230 | MPa | ISO 527-2 |
| 121°C | 155 | 145 | MPa | ISO 527-2 |
| Tensile Strength | ASTM D638, ISO 527-2 | |||
| Yield, -40°C | 83.0 | 104 | MPa | ASTM D638, ISO 527-2 |
| Yield, 23°C | 34.0 | 26.0 | MPa | ASTM D638, ISO 527-2 |
| Yield, 80°C | 15.0 | -- | MPa | ASTM D638, ISO 527-2 |
| Yield, 121°C | 12.0 | -- | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation | ||||
| Yield, 23°C | 30 | -- | % | ASTM D638 |
| Yield, 23°C | 7.0 | 30 | % | ISO 527-2 |
| Fracture, 23°C | > 100 | -- | % | ASTM D638 |
| Nominal Tensile Strain at Break (23°C) | > 50 | > 50 | % | ISO 527-2 |
| Flexural Modulus | ||||
| 23°C | 610 | -- | MPa | ASTM D790 |
| 23°C | 750 | -- | MPa | ISO 178 |
| Flexural Strength (23°C) | 28.0 | -- | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ||||
| 23°C | 640 | -- | J/m | ASTM D256 |
| -40°C | 6.0 | -- | kJ/m² | ISO 180 |
| 23°C | No Break | -- | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, not annealed | 124 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 47.0 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 43.0 | -- | °C | ISO 75-2/A |
| Peak Melting Temperature | 220 | -- | °C | ASTM D3418, ISO 3146 |
| Linear thermal expansion coefficient | ||||
| Flow | 1.2E-4 | -- | cm/cm/°C | ASTM E831 |
| Flow | 9.3E-5 | -- | cm/cm/°C | |
| Lateral | 1.1E-4 | -- | cm/cm/°C | |
| RTI Elec | UL 746 | |||
| 1.50 mm | 65.0 | -- | °C | UL 746 |
| 3.00 mm | 65.0 | -- | °C | UL 746 |
| RTI Imp | UL 746 | |||
| 1.50 mm | 65.0 | -- | °C | UL 746 |
| 3.00 mm | 65.0 | -- | °C | UL 746 |
| RTI | UL 746 | |||
| 1.50 mm | 65.0 | -- | °C | UL 746 |
| 3.00 mm | 65.0 | -- | °C | UL 746 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | ||||
| 1.50 mm | > 1.0E+13 | -- | ohms·cm | ASTM D257 |
| -- | > 1.0E+13 | -- | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.50 mm | HB | -- | UL 94 | |
| 3.00 mm | HB | -- | UL 94 |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 65.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Cylinder Zone 1 Temp. | 245 - 255 | °C | |
| Cylinder Zone 3 Temp. | 245 - 260 | °C | |
| Cylinder Zone 5 Temp. | 240 - 250 | °C | |
| Flange temperature | 230 - 245 | °C | |
| Head Temperature | 230 - 245 | °C | |
| Extruder Screw L/D Ratio | 20.0:1.0 to 24.0:1.0 | ||
| Extruder Screw Compression Ratio | 3.5:1.0 to 4.0:1.0 | ||
| Melt Temperature | 240 - 250 | °C | |
| Die Temperature | 230 - 245 | °C |
| Extrusion instructions |
|---|
| Screw Parameters Metering Section : 40% Transition Section : 3 to 4 flights Feed Section : balance of screw length |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vydyne® 21ZLV | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| EVALENE® PP PHY0351 | JG Summit Petrochemical Corporation | PP Homopolymer | EVALENE® PP |
| HIPOL™ F600 | Mitsui Chemicals, Inc. | PP, Unspecified | HIPOL™ |
| LNP™ LUBRICOMP™ DFL36E compound | SABIC Innovative Plastics Europe | PC | LNP™ LUBRICOMP™ |
| Sylvin 9067-85 Yellow 4127 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |