Latigray 82-03 CW/95
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latigray |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | p6QMrH_Latigray-82-03-CW-95.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Radiopaque compound based on Polyamide 12 (PA 12). Metallic filler. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 8.58 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.50 to 0.90 | % | |
| Flow : 2.00 mm | 0.50 to 0.90 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 6700 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 40.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 1.2 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 2(23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 3(23°C) | 20 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact 4(23°C) | 85 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 155 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 105 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 165 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 70 | ohms | ASTM D257 |
| Volume Resistivity | 7.0E+2 | ohms·cm | ASTM D257 |
| Electromagnetic Reflection | 95.0 | dB | ASTM EST-83 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Half Value Thickness | Internal Method | ||
| -- 5 | 560.0 | µm | |
| -- 6 | 140.0 | µm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 80x10x4 mm |
| 3 . | 80x10x4 mm |
| 4 . | 63.5x12.7x3.2 mm |
| 5 . | 120 kV |
| 6 . | 80 kV |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PC PC0700 resin | SABIC Innovative Plastics Asia Pacific | PC | SABIC® PC |
| Amodel® DW-1150 | Solvay Specialty Polymers | PPA | Amodel® |
| Fainplast PVC MPH 73/GT 1 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| DJSilicone NE-5170 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| DAI-EL™ G-551 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |