InnoPlus LL7910A
| Category: | mLLDPE , Metallocene Linear Low Density Polyethylene |
| Manufacturer: | PTT Global Chemical Public Company Limited |
| Trademark: | InnoPlus |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | p6HUNm_InnoPlus-LL7910A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
InnoPlus LL7910A resin is a metallocene polyethylene with hexene comonomers, without slip and antiblock. This grade is an easy processing grade which offers an outstanding balance between processing and film properties. Films extruded from InnoPlus LL7910A have high tensile and dart Impact strength properties. It is suitable for both blown film and cast film processing. InnoPlus LL7910A is recommended for producing the heavy duty films, stretch films, shrink films, lamination films, liners, food packagings, multi-layer packaging films and freezer packaging films. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 25 µm, Blown Film | 191 | MPa | |
| 1% Secant, TD : 25 µm, Blown Film | 224 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 25 µm, Blown Film | 60.0 | MPa | |
| TD : Break, 25 µm, Blown Film | 53.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm, Blown Film | 490 | % | |
| TD : Break, 25 µm, Blown Film | 680 | % | |
| Dart Drop Impact (25 µm, Blown Film) | 210 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, Blown Film | 110 | g | |
| TD : 25 µm, Blown Film | 570 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 107 | °C | ASTM D1525 |
| Peak Melting Temperature | 114 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 62 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 8.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 to 180 | °C | |
| Die Temperature | 170 to 190 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEFTEKHIM PP 4341S | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| BJB Polyurethane ST-1060 A/B | BJB Enterprises, Inc. | TSU | BJB Polyurethane |
| FORMULA P ELAN XP 422 | Putsch Kunststoffe GmbH | PP+Styrenic | FORMULA P |
| Huafon JF-W-3025 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| TOTAL Polypropylene PPH 3927WZ | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |