30% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. NSF 51 listing, WRAS certification, KTW certification in recognized colors.

General Information
Filler / Reinforcement	Glass Fiber, 30% Filler by Weight
Features	ECO Compliant
Agency Ratings	EU Eco NSF 51 WRAS Unspecified Rating
Processing Method	Injection Molding
Multi-Point Data	Coefficient of Thermal Expansion vs. Temperature (ASTM E831) Elastic Modulus vs Temperature (ASTM D4065) Flexural DMA (ASTM D4065) Instrumented Impact (Energy) (ASTM D3763) Instrumented Impact (Load) (ASTM D3763) Pressure-Volume-Temperature (PVT - Zoller Method) Shear DMA (ASTM D4065) Specific Heat vs. Temperature (ASTM D3417) Tensile Fatigue Tensile Stress vs. Strain (ASTM D638) Thermal Conductivity vs. Temperature (ASTM E1530) Viscosity vs. Shear Rate (ASTM D3835)

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.51	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (337°C/6.6 kg)	5.0	g/10 min	ASTM D1238
Molding Shrinkage			Internal Method
Flow : 3.20 mm	0.20 to 0.40	%
Across Flow : 3.20 mm	0.20 to 0.40	%
Water Absorption			ASTM D570
24 hr	0.16	%
Equilibrium, 23°C	0.90	%

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (M-Scale)	114		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus ¹	9310	MPa	ASTM D638
Tensile Strength ²			ASTM D638
Yield	169	MPa
Break	159	MPa
Tensile Elongation ³(Break)	3.0	%	ASTM D638
Flexural Modulus ⁴(100 mm Span)	8960	MPa	ASTM D790
Flexural Strength ⁵(Break, 100 mm Span)	228	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C)	85	J/m	ASTM D256
Unnotched Izod Impact (23°C)	430	J/m	ASTM D4812
Reverse Notch Izod Impact (3.20 mm)	490	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
0.45 MPa, Unannealed, 6.40 mm	212	°C
1.8 MPa, Unannealed, 6.40 mm	210	°C
Vicat Softening Temperature	228	°C	ASTM D1525 ⁶
CLTE - Flow (-20 to 150°C)	2.0E-5	cm/cm/°C	ASTM E831
RTI Elec	180	°C	UL 746
RTI Imp	170	°C	UL 746
RTI Str	180	°C	UL 746

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	3.0E+16	ohms·cm	ASTM D257
Dielectric Strength			ASTM D149
1.60 mm, in Air	25	kV/mm
1.60 mm, in Oil	30	kV/mm
Dielectric Constant (1 kHz)	3.70		ASTM D150
Dissipation Factor			ASTM D150
1 kHz	1.5E-3
2.45 GHz	5.3E-3
Arc Resistance ⁷	PLC 6		ASTM D495
Comparative Tracking Index (CTI)	PLC 4		UL 746
High Amp Arc Ignition (HAI)	PLC 4		UL 746
High Voltage Arc Tracking Rate (HVTR)	PLC 3		UL 746
Hot-wire Ignition (HWI)	PLC 1		UL 746

Flammability	Nominal Value	Unit	Test Method
Flame Rating			UL 94
0.254 mm	V-0
1.22 mm	5VA
Oxygen Index	50	%	ASTM D2863
NBS Smoke Density - Flaming, Ds, 4 min	1.60		ASTM E662

Injection	Nominal Value	Unit
Drying Temperature	149	°C
Drying Time	4.0 to 6.0	hr
Drying Time, Maximum	24	hr
Suggested Max Moisture	0.020	%
Suggested Shot Size	40 to 60	%
Rear Temperature	332 to 399	°C
Middle Temperature	338 to 399	°C
Front Temperature	343 to 399	°C
Nozzle Temperature	343 to 399	°C
Processing (Melt) Temp	349 to 399	°C
Mold Temperature	135 to 163	°C
Back Pressure	0.345 to 0.689	MPa
Screw Speed	40 to 70	rpm
Vent Depth	0.025 to 0.076	mm

Note Message
1 .	5.0 mm/min
2 .	Type I, 5.0 mm/min
3 .	Type I, 5.0 mm/min
4 .	2.6 mm/min
5 .	2.6 mm/min
6 .	Rate B (120°C/h), Loading 2 (50 N)
7 .	Tungsten Electrode

Resin Grade	Manufacturer	Category	Trademark
POLYshine PBT D223 GF15 FR	Polykemi AB	PBT	POLYshine
Unichem 8818	Colorite Polymers	PVC, Unspecified	Unichem
Diablend 4500	DTR S.r.l. (Develop Thermoplastic Resins)	PC+ABS	Diablend
Fluon® PTFE G340	Asahi Glass Co., Ltd.	PTFE	Fluon®
LNP™ THERMOCOMP™ RC004SXS compound	SABIC Innovative Plastics	Nylon 66	LNP™ THERMOCOMP™