Zislloy® BFG30-BN00N2
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Zig Sheng Industrial Co., Ltd. |
| Trademark: | Zislloy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | p5T6IC_Zislloy-BFG30-BN00N2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6 injection molding grade, 30% glass fiber reinforced, natural color. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 80°C, 2.00 mm | 0.70 | % | |
| Flow : 80°C, 2.00 mm | 0.30 | % | |
| Water Absorption (Saturation, 23°C) | 0.90 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 93 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9300 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 180 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.5 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 8300 | MPa | ISO 178 |
| Flexural Stress 3 | 275 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 13 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 93 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C) | 13 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 210 | °C | ISO 75-2/A |
| Melting Temperature 4 | 220 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 550 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time - Hot Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 265 to 280 | °C | |
| Mold Temperature | 80.0 to 120 | °C | |
| Residual Moisture Content | < 0.10 | % | Karl Fisher |
| Note Message | |
|---|---|
| 1 . | 60x60x2 mm |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUMILITE® PVC VSS-1202 | Sumitomo Bakelite Co., Ltd. | PVC, Unspecified | SUMILITE® PVC |
| SUMIKASUPER® LCP E6606 | Sumitomo Chemical Co., Ltd. | LCP | SUMIKASUPER® LCP |
| NOVALAC FM 1132P | Vyncolit N.V. | Phenolic | NOVALAC |
| Colorite CS Series CS8042SC | Colorite Polymers | PVC, Flexible | Colorite CS Series |
| Hostacom D1179 0907 | LyondellBasell Industries | PP Impact Copolymer | Hostacom |