Crastin® S600F20 NC010
| Category: | PBT , THERMOPLASTIC POLYESTER RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Crastin® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | p4Zxnw_Crastin-S600F20-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unreinforced Medium Viscosity Polybutylene Terephthalate |
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.31 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 19 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.6 | % | |
| Flow | 1.7 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 2.00 mm | 0.40 | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.20 | % | |
| Viscosity Number | 130 | cm³/g | ISO 307 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2600 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 58.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 7.0 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 40 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 2600 | MPa | |
| 1000 hr | 1800 | MPa | |
| Flexural Modulus | 2200 | MPa | ISO 178 |
| Flexural Stress | 85.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m² | |
| 23°C | 5.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength (23°C) | 4.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 115 | °C | ISO 75-2/B |
| 0.45 MPa, Annealed | 180 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 50.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 60.0 | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 55.0 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 175 | °C | ISO 306/B50 |
| Melting Temperature 2 | 225 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.1E-4 | cm/cm/°C | |
| Transverse | 1.2E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 26 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.80 | ||
| 1 MHz | 3.20 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 2.0E-3 | ||
| 1 MHz | 0.020 | ||
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.800 mm | HB | ||
| 1.50 mm | HB | ||
| Oxygen Index | 22 | % | ISO 4589-2 |
| Fogging - G-value (condensate) | 0.0 | g | ISO 6452 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Heat Capacity of Melt | 2110 | J/kg/°C | |
| Thermal Conductivity of Melt | 0.21 | W/m/K |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Odor | 3 | VDA 270 | |
| Thermal Desorption Analysis of Organic Emissions - AMax | 1.00 | µg/g | VDA 278 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Density | 1.11 | g/cm³ |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BIOH™ Polyol X-0005 | Cargill Industrial Bio-Products | Biodeg Polymers | BIOH™ Polyol |
| Buna® EP G 8850 | LANXESS Corporation | EPDM | Buna® EP |
| Arnitel® UM551 | DSM Engineering Plastics | TPC-ES | Arnitel® |
| KOPA® KN163HI | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| Karina WHITE PVC COMPOUND -E 835-10/155-C-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |