Staramide BG4ST43
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Staramide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | p4BiEA_Staramide-BG4ST43.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Staramide BG4ST43 is an Impact Modified and Glass Fiber Reinforced Polyamide 6 Injection Molding Resin |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 0.70 to 0.90 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 6.0 | % | |
| Equilibrium, 23°C, 50% RH | 1.4 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 101 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5000 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 85.0 | MPa | |
| Break | 83.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 3.2 | % | |
| Break | 4.0 | % | |
| Flexural Modulus 2 | 4000 | MPa | ISO 178 |
| Flexural Stress | 115 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 31.0 | mg | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179/1eA | ||
| -30°C | 12 | kJ/m² | |
| 23°C | 17 | kJ/m² | |
| Charpy Unnotched Impact Strength 4 | ISO 179/1eU | ||
| -30°C | 60 | kJ/m² | |
| 23°C | 50 | kJ/m² | |
| Notched Izod Impact Strength 5 | ISO 180/1A | ||
| -40°C | 12 | kJ/m² | |
| -30°C | 12 | kJ/m² | |
| -20°C | 14 | kJ/m² | |
| 23°C | 18 | kJ/m² | |
| Unnotched Izod Impact Strength 6 | ISO 180/1U | ||
| -30°C | 55 | kJ/m² | |
| 23°C | 45 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 7 | |||
| 0.45 MPa, Unannealed, 100 mm Span | 205 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 100 mm Span | 175 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 185 | °C | ISO 306/B50 |
| -- | 186 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 4.0E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 1.8E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 550 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm, Tested by E2P) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 230 to 240 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 240 to 260 | °C | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 sp=62mm |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 |
| 7 . | 120*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinko-Lac® ASA E310 | Mitsubishi Rayon America Inc. | ASA | Shinko-Lac® |
| Tuftec™ H1043 | AKelastomers | SEBS | Tuftec™ |
| CALIBRE™ 603-6 | Trinseo | PC | CALIBRE™ |
| Karina WHITE PVC COMPOUND 812-10/ 55-AY-ERYB-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Pinnacle PP 1112 | Pinnacle Polymers | PP Homopolymer | Pinnacle PP |