Durolon® G2530 PR001
| Category: | PC , Polycarbonate |
| Manufacturer: | Unigel Plásticos |
| Trademark: | Durolon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | p3ssLH_Durolon-G2530-PR001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Durolon® G2530 PR001 is a Polycarbonate (PC) material filled with 30% glass fiber. It is available in Europe, Latin America, or North America for injection molding. Important attributes of Durolon® G2530 PR001 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow | 0.15 to 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.11 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 92 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8100 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Break) | 120 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 8530 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 170 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 160 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 144 | °C | ASTM D648, ISO 75-2/A |
| CLTE - Flow | 2.3E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm) | 22 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 60 Hz | 3.10 | ||
| 1 MHz | 2.95 | ||
| Dissipation Factor | ASTM D150 | ||
| 60 Hz | 8.0E-4 | ||
| 1 MHz | 9.0E-3 | ||
| Arc Resistance | 110 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Ignition Temperature (3.20 mm) | 960 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 270 | °C | |
| Middle Temperature | 280 | °C | |
| Front Temperature | 290 | °C | |
| Nozzle Temperature | 280 | °C | |
| Processing (Melt) Temp | 240 to 300 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 90910CSU05 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| Niretan B SV10 | Soredi S.p.a. | Nylon 6 | Niretan B |
| Celstran® TPU-GF50-01 | Celanese Corporation | TPU, Unspecified | Celstran® |
| ENVIROLON® ENV1266G33-NAT | ENVIROPLAS®, Inc. | Nylon 66 | ENVIROLON® |
| Sylvin 8980-80 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |