DESLEN™ DSC502G6
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | DESCO Co., Ltd. |
| Trademark: | DESLEN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | p3T4Lb_DESLEN-DSC502G6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Descriptions: DESLEN™ DSC502G6 is Polypropylene Glass Filler 30% reinforced resin. It has good rigidity and Impact resistance. Applications: DESLEN™ DSC502G6 has good mechanical property and rigidity and it is applied to air cleaner case, blower fan and electronic parts and automotive parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 - 0.50 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 78.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 8.0 | % | ASTM D638 |
| Flexural Modulus | 5880 | MPa | ASTM D790 |
| Flexural Strength | 118 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 98 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 157 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 140 | °C | ASTM D648 |
| Melting Temperature | 163 | °C | DSC |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | < 0.20 | % | |
| Rear Temperature | 190 - 200 | °C | |
| Middle Temperature | 200 - 210 | °C | |
| Front Temperature | 200 - 220 | °C | |
| Nozzle Temperature | 200 - 220 | °C | |
| Processing (Melt) Temp | 200 - 220 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C |
| Injection instructions |
|---|
| Speed: 40 to 70%Pressure 1st: 30 to 60%Pressure 2nd: 30 to 60Holding Pressure: 10 to 20% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® S CP300 100 NAT | Radici Plastics | Nylon 6 | Radilon® |
| tefanyl® VE VEIP 220 | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | tefanyl® VE |
| Trexprene® D50CI | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| COSMOTHENE® L705 | TPC, The Polyolefin Company (Singapore) Pte Ltd | LDPE | COSMOTHENE® |
| Flontech® FT-CAR23-GR2-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |